TEDUR® L 9114-1 S
- Chemical Family
- Polyphenylene Sulfide (PPS)
MOCOM Compounds TEDUR® L 9114-1 S is a base polymer of Polyphenylene Sulfide containing 60% glass fibers, offering high stiffness and injection molding grade. It is suitable for various applications and should be stored in a dry, light-protected environment not exceeding 30°C. During processing injection molding, melt temperature should be 320-340°C and mold temperature should be greater than 140°C. Ensure that the temperature is not exceeded, otherwise the material may degrade.
Product families
- High Performance Thermoplastics
Other characteristics
- Brand
- TEDUR
- Polymer Name
- Polyphenylene Sulfide (PPS)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 23000.0 - 23000.0 MPa
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Chemical Resistant
- Good Flow
- High Stiffness
- High Temperature Resistance
- Low Thermal Expansion
- Wide Temperature Operating Range
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 130-140 °C for 2-4 h; Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Pressure Vessel
- Pump Housing
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 23000.0 | MPa | ISO 178 |
| Flexural Strength | 300.0 | MPa | ISO 178 |
| Tensile Modulus | 24000.0 | MPa | ISO 527 |
| Flexural Deflection (Maximum Force) | 1.4 | % | ISO 178 |
| Tensile Strength at Break | 185.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 1.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 35.0 | kJ/m² | ISO 179/1eU |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1900.0 | kg/m³ | ISO 1183 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (1.8 MPa) | 280.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 280.0 | °C | ISO 11357 |
Table 4 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistance | 1 x 10¹² | Ohm | DIN EN 62631-3-2 |
Table 5 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (1.5 mm) | V - 0 | class | UL 94 |
| Glow Wire (GWFI, 960°C, 2mm) | Passed | — | DIN EN 60695 |
Table 6 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Mould Temperature | min. 140 | °C |
| Melt Temperature | 320 - 340 | °C |