Adhesives Technology ACCU-CHOCK
- Chemical Family
- Epoxy & Epoxy Derivatives
Adhesives Technology ACCU-CHOCK is a two-component, high-performance, high early and ultimate strength epoxy machine chock for use in high bearing areas with negligible shrinkage and creep, fast cure and excellent flowability. The recommended application temperature range is between 60°F - 95°F (16°C - 35°C).
Product families
Applications
- Equipment & Parts
Product Families
- Mortar & Grouts
Other characteristics
- Features
Chemical Resistant, Creep Resistant, Fast Cure, High Flowability, High Performance, High Strength, Low Exotherm, Low Shrinkage, Low Toxicity, Oil Resistant
- Product Type
- 2K (2 component) Adhesive
- Markets
- Industrial
- Clean Up
Always wear appropriate personal protective equipment such as safety glasses and gloves. Clean uncured materials from tools and equipment using a mild solvent, such as a citrus based product or denatured alcohol. Cured material may only be removed mechanically using a sander or grinder.
- Availability
Adhesives Technology Corp. (ATC) products are available online and through select distributors providing all your construction needs.
- Technology
- Ready-to-Use Products
- Shelf Life Storage
For best results, store between 40°F (4°C) and 95°F (35°C). Shelf life is 24 months when stored in unopened containers in dry conditions.
- Advantages and Features
Designed for use in dynamic and high-impact shock loading; Precision grouting with negligible shrinkage and creep; High early strength; Highest effective bearing area (over 98%); Low exotherm for deep pour capability; Excellent oil and chemical resistance; Superior flowability; Ready to mix - pre-measured units; Low toxicity; Easy soap and water clean up; Designed for dynamic and static loading; Made in the USA
- Limitations and Warnings
For professional use only; Do not thin with solvents, as this will prevent cure; Do not mix partial kits; All metal surfaces that come in contact with ACCU-CHOCK should be sandblasted to white metal finish and wiped clean with solvent; All concrete surface contaminations must be removed by mechanical means creating a surface profile of exposed sound aggregate.; Typical grouting depth is 1 to 3 in.; Maximum pour depth is 3 in. - contact ATC for pour depths greater than 3 in.; Substrate temperature should be a minimum of 50°F (10°C)
- Installation and Coverage
In order to achieve maximum results, proper installation is imperative.
- General Uses and Applications
High stress machine base plate chock for use in heavy equipment industries such as wind farms, gas transmission, chemical processing and refineries, paper mills, steel rail and marine facilities.. New equipment installation and quick re-grouting of applications subject to chemical attack.
- Ready to Use Product Features
- Chemical Resistant
- Creep Resistant
- Fast Cure
- High Flowability
- High Performance
- High Strength
- Low Exotherm
- Low Shrinkage
Technical data
Table 1 of 1
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Bond Strength | 3000 (20.7) | psi (MPa) | C882 |
| Coefficient of Thermal Expansion | 18x10^{-6} | in./(in.-°F) | C531 |
| Compressive Modulus | 2300000 (15,858) | psi (MPa) | D695 |
| Compressive Strength | 16250 (112) | psi (MPa) | C579 |
| Fire Resistance | Self-Extinguishing | — | D635 |
| Flexural Strength | 6,000 (41.4) | psi (MPa) | C580 |
| Gel Time | 60.0 | min | C881 |
| Linear Shrinkage on Cure | 0.02 | % | C531 |
| Modulus of Elasticity | 2,400,000 (16,547) | psi (MPa) | C580 |
| Shore D Hardness | 90.0 | — | D2240 |
| Shrinkage | Pass | — | C883 |
| Tensile Modulus of Elasticity | 2400000 (16,547) | psi (MPa) | C580 |