CRACKBOND® 2100 MV Class B
CRACKBOND® 2100 MV Class B and 2100 MVLPL (Long Pot Life) products are two-component, high strength epoxy adhesives that are ideal for bonding fresh to hardened concrete or perfect for use in a variety of repair projects. CRACKBOND 2100 MV may be used in temperatures between 40°F and 100°F (4°C and 38°C), while CRACKBOND 2100 MV-LPL, with its slower cure rate, may be used in temperatures between 60°F and 110°F (16°C and 43°C).
Product families
- Structural Adhesives
Other characteristics
- Brand
- CRACKBOND
- Product Type
2K (2 component) Adhesive, Epoxy Adhesive, Structural Adhesive; 2K (2 component) Adhesive; Epoxy Adhesive; Structural Adhesive
- Compatible Substrates & Surfaces
- Concrete, Metal, Steel
- Markets
- Adhesives & Sealants
- Building & Construction
- Industrial
- Paints & Coatings
- Clean Up
Always wear appropriate protective equipment such as safety glasses and gloves. Clean uncured materials from tools and equipment with mild solvent. Cured material can only be removed mechanically.
- Availability
Adhesives Technology Corp. (ATC) products are available online and through select distributors providing all your construction needs.
- Technology
- Ready-to-Use Products
- Specification
The bonding agent shall be a twocomponent, 1:1 mix ratio epoxy system supplied in premeasured containers. CRACKBOND 2100 MV, when cured 7 days and at a minimum temperature of 75 °F (24 °C), shall have a minimum compressive yield strength of 12,580 psi (86.7 MPa) and a minimum compressive modulus of 460,700 psi (3,176 MPa) per ASTM D695. CRACKBOND 2100 MV-LPL, when cured 7 days and at a minimum temperature of 75 °F (24 °C), shall have a minimum compressive yield strength of 10,250 psi (70.7 MPa) and a minimum compressive modulus of 503,100 psi (3,469 MPa) per ASTM D695. The bonding agent shall be CRACKBOND 2100 MV or CRACKBOND 2100 MV-LPL from Adhesives Technology Corp., Pompano Beach, Florida.
- Shelf Life Storage
24 months when stored in unopened bulk containers in dry conditions. The 8.6 fl. oz. (254 ml) cartridge shelf life is 12 months when stored in unopened containers in dry conditions. Store between 40°F (4°C) and 95°F (35°C).
- Advantages and Features
NSF/ANSI 61 & 372 Drinking Water System Components; Available packaging in cartridges and bulk; red basecoat available in 4 gallon kits only
- Standards and Approvals
- ASTM C881-15/AASHTO M235
- CRACKBOND 2100 MV
- Type I*, II, IV* & V* Grade 2 Class B
- Type I**, II, IV* & V* Grade 2 Class C
- Drinking Water System Components
- NSF/ANSI 61 & 372
- CRACKBOND 2100 MV-LPL
- Type I, II, IV* & V** Grade 2 Class C
Technical data
Table 1 of 1
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water Absorption (14 day, 40°F) | 0.1 | % | D570 |
| Bond Strength Hardened to Hardened Concrete (2 day, 40°F) | 2,380 (16.4) | psi (MPa) | C882 |
| Bond Strength Hardened to Hardened Concrete (2 day, 40°F) | 3,020 (20.8) | psi (MPa) | C882 |
| Bond Strength Fresh to Hardened Concrete (14 day, 40°F) | 2030 (14.0) | psi (MPa) | C882 |
| Compressive Modulus (7 day, 40°F) | 476000 (3,282) | psi (MPa) | D695 |
| Compressive Yield Strength (7 day, 40°F) | 11340 (78.2) | psi (MPa) | D695 |
| Consistency or Viscosity (40°F) | 17000.0 | cP | C881 |
| Gel Time - 60 Gram Mass (40°F) | 199.0 | min | C881 |
| Heat Deflection Temperature (7 day, 40°F) | 126 (52.2) | °F (°C) | D648 |
| Linear Coefficient of Shrinkage (2 day, 40°F) | 0.00015 | % | D2566 |
| Pot Life (1 Gallon, 40°F) | 37.0 | min | — |
| Tack-Free Time | 7.16 | hr | D2377 |