CRACKBOND® 2100 MV-LPL
CRACKBOND® 2100 MV (Medium Viscosity) and CRACKBOND® 2100 MV-LPL products are two-component, high strength epoxy adhesives that are ideal for bonding fresh to hardened concrete or perfect for use in a variety of repair projects. CRACKBOND 2100 MV may be used in temperatures between 40°F and 100°F (4°C and 38°C), while CRACKBOND 2100 MV-LPL, with its slower cure rate, may be used in temperatures between 60°F and 110°F (16°C and 43°C).
Product families
- Structural Adhesives
Other characteristics
- Brand
- CRACKBOND
- Product Type
2K (2 component) Adhesive, Epoxy Adhesive, Structural Adhesive; 2K (2 component) Adhesive; Epoxy Adhesive; Structural Adhesive
- Compatible Substrates & Surfaces
- Concrete, Metal, Steel
- Markets
- Adhesives & Sealants
- Building & Construction
- Industrial
- Paints & Coatings
- Clean Up
Always wear appropriate protective equipment such as safety glasses and gloves. Clean uncured materials from tools and equipment with mild solvent. Cured material can only be removed mechanically.
- Availability
Adhesives Technology Corp. (ATC) products are available online and through select distributors providing all your construction needs.
- Technology
- Ready-to-Use Products
- Specification
The bonding agent shall be a twocomponent, 1:1 mix ratio epoxy system supplied in premeasured containers. CRACKBOND 2100 MV, when cured 7 days and at a minimum temperature of 75 °F (24 °C), shall have a minimum compressive yield strength of 12,580 psi (86.7 MPa) and a minimum compressive modulus of 460,700 psi (3,176 MPa) per ASTM D695. CRACKBOND 2100 MV-LPL, when cured 7 days and at a minimum temperature of 75 °F (24 °C), shall have a minimum compressive yield strength of 10,250 psi (70.7 MPa) and a minimum compressive modulus of 503,100 psi (3,469 MPa) per ASTM D695. The bonding agent shall be CRACKBOND 2100 MV or CRACKBOND 2100 MV-LPL from Adhesives Technology Corp., Pompano Beach, Florida.
- Shelf Life Storage
24 months when stored in unopened bulk containers in dry conditions. The 8.6 fl. oz. (254 ml) cartridge shelf life is 12 months when stored in unopened containers in dry conditions. Store between 40°F (4°C) and 95°F (35°C).
- Advantages and Features
Extended working time with new higher strength formula
- Standards and Approvals
- ASTM C881-15/AASHTO M235
- CRACKBOND 2100 MV
- Type I*, II, IV* & V* Grade 2 Class B
- Type I**, II, IV* & V* Grade 2 Class C
- Drinking Water System Components
- NSF/ANSI 61 & 372
- CRACKBOND 2100 MV-LPL
- Type I, II, IV* & V** Grade 2 Class C
- Limitations and Warnings
Do not thin with solvents, as this may affect cure.. Not recommended for any anchoring and doweling application where there may be a sustained tensile load, including overhead applications.
Technical data
Table 1 of 1
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Bond Strength Fresh Concrete to Steel (14 day, 75°F) | 2,300 (15.9) | psi (MPa) | C882 |
| Bond Strength Fresh to Hardened Concrete (14 day, 75°F) | 2,680 (18.5) | psi (MPa) | C882 |
| Bond Strength Hardened to Hardened Concrete (14 day, 75°F) | 3,450 (23.8) | psi (MPa) | C882 |
| Compressive Modulus (7 day, 75°F) | 503,100 (3,469) | psi (MPa) | D695 |
| Compressive Yield Strength (7 day, 75°F) | 10,250 (70.7) | psi (MPa) | D695 |
| Consistency or Viscosity (75°F) | 3980.0 | cP | C881 |
| Gel Time - 60 Gram Mass (75°F) | 105.0 | min | C881 |
| Heat Deflection Temperature (7 day, 75°F) | 129 (53.9) | °F (°C) | D648 |
| Linear Coefficient of Shrinkage (2 day, 75°F) | 0.0002 | % | D2566 |
| Pot Life (1 Gallon, 75°F) | 52.0 | min | — |
| Tack-Free Time | 6.25 | hr | D2377 |
| Tensile Elongation (7 day, 75°F) | 3.0 | % | D638 |