SYNTHALAT A 1633
- CASE Ingredients Functions
- Binder & Resin
- Chemical Family
- Acrylics & Acrylates
SYNTHALAT A 1633 is an acrylic resin cross-linked with polyisocyanate. It is used in combination with aromatic and aliphatic polyisocyanates for fast-drying 2-component polyurethane coatings, particularly for coating furniture. It is a fast-drying polymethacrylate that permits the manufacture of very quick-drying 2-component coating systems. These coatings are suitable for industrial furniture coatings and other wood coatings. It has applications in wood flooring, metal coatings, furniture coatings, and other printing applications.
Product families
- Acrylics
Other characteristics
- Brand
- SYNTHALAT
- End Uses
- 2K (2 component) Coating
- Compatible Substrates & Surfaces
- Glass, Metal, Paper, Plastics, Wood
- Carrier
- Solvent-based
- Markets
- Adhesives & Sealants
- Building & Construction
- Consumer Goods
- Paints & Coatings
- Printing & Packaging
- Cure
- Chemical Cure
- Supplied As
A = 50% in xylene/butyl acetate (1:1) B = 50% in butyl acetate C = 50% in shellsol A/ethoxy propyl acetate (3:1)
- Technology
- CASE Ingredients
- Labeling Claims
- APEO-Free
- Formaldehyde-free
- Plasticizer-free
- Coating End Applications
- 2K (2 component) Coating
- Compatible Substrates and Surfaces
- Glass
- Metal
- Paper
- Plastics
- Wood
- Mixing ratio with poly-isocyanates
Assuming equivalent reaction of the reactive groups (NCO : OH = 1:1), the following formula applies for calculation of the amount of polyisocyanate to be added (relative to 100 parts by weight of SYNTHALAT-A 1633, solid): 42 X 100 X 2,0 17 X NCO % 42 = molecular weight of the NCO group 17 = molecular weight of the OH group
Technical data
Table 1 of 1
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Non Volatile Content | 50.0 | w % | AV-F-F003 |
| Color | max. 2 | Gardner | AV-F-F007 |
| Density | 0.994 | g/ml | AV-F-0D001 |
| Flash Point | 21.0 | °C | AV-F-f006 |
| Flow Time | 160-200 | seconds | AV-F-V003 |
| Hydroxyl Content | 60-75 | % | AV-F-H003 |
| Hydroxyl Content | 2.0 | % | Relative to NVC |