Melos PC 51-040
- Chemical Family
- Polyurethanes (PU)
Melos PC 51-040 is a solvent-free, two-component polyurethane-based coating. PC 51-040 has excellent bonding properties to base surfaces and PUR mastic compounds.
Product families
- Other Paints & Coatings
Other characteristics
- Features
- Abrasion Resistant
- Product Type
2K (2 component) Coating, Solventless & High Solids Coating; 2K (2 component) Coating; Solventless & High Solids Coating
- Markets
- Paints & Coatings
- Storage
PC 51-040 should be kept in a dry and cool place. Shelf life of product stored in unopened original containers is 6 months, contents must be protected against moisture. After prolonged storage the suitability of PC 51-040 needs to be examined. Open containers have to be closed carefully, protected against moisture and used as soon as possible.
- PACKAGING
- Part A
- 240 kg drums
- Part B
- 210 kg drums
- Applications
Paints & Coatings — Other Paints & Coatings Applications
- Technology
- Ready-to-Use Products
- Packaging Type
- Drums
- Labeling Claims
- Solvent-free
- Safety Guidelines
PC 51-040 must be stored dry and cool. Avoid contact with water when the component A has been mixed with the component B, there may otherwise form foam.
- Installation Guidelines
PC 51-040 A-component is ready for use and should be homogenized before processing only. PC 51-040 A- and B-components are stirred in the described mixing ratio in a mixer for 3-5 minutes. In order to exclude mixing errors the mixture should be poured into a new, clean container and mixed again for 1 - 2 minutes. After the mixing, PC 51-040 is applied to the pre-treated substrate with a squeegee. The tooth size should be selected according to the thickness of the required layer.
- Certifications and Compliance
- ISO 14001
- ISO 45001
- ISO 50001
- ISO 9001
- Ready to Use Product Features
- Abrasion Resistant
Technical data
Table 1 of 1
7 rows| Characteristic | Value | Unit |
|---|---|---|
| Density (at 20°C) (Mixture) | 1.19 | g/cm³ |
| Viscosity (at 20°C) (Part A) | 12000 ± 1000 | mPas |
| Viscosity (at 20°C) (Part B) | 5000 ± 500 | mPas |
| Mixing Ratio Part A : Part B (By Volume) | 1 : 1 | — |
| Mixing Ratio (Part A : Part B (By Weight)) | 1 : 0,9 | — |
| Pot Life | 45 ± 10 | Minutes |
| Processing Temperature | min. 10 | °C |