Melos PC 51-010
- Chemical Family
- Polyurethanes (PU)
Melos PC 51-010 is a solvent-free, flexible, two-component polyurethane-based indoor coating. PC 51-010 has an excellent tack to base layers and PUR trowelled compounds.
Product families
- Other Paints & Coatings
Other characteristics
- Features
Abrasion Resistant, Good Adhesion, Improved Flexibility
- Product Type
2K (2 component) Coating, Solventless & High Solids Coating; 2K (2 component) Coating; Solventless & High Solids Coating
- Application Method
- Spray
- Markets
- Paints & Coatings
- Storage
Store in a dry and cool place, protect from moisture. Shelf life of the product stored in unopened original containers is 6 months. After prolonged storage the suitability of PC 51-010 needs to be examined.
- PACKAGING
- Part A
- 15,7 kg Container
- Part B
- 4,4 kg Container
- Applications
Paints & Coatings — Other Paints & Coatings Applications
- Technology
- Ready-to-Use Products
- Labeling Claims
- Solvent-free
- Safety Guidelines
PC 51-010 must be stored dry and cool. Avoid contact with water when the component A has been mixed with the component B, there may otherwise form foam. Use safety goggles and gauntlets when handling. Avoid breathing the fumes, since isocyanate can irritate mucous membranes.
- Application Methods
- Spray
- Installation Guidelines
Mix components A and B in the prescribed blend ratio for 3-5 minutes using a powered agitator. Intensive mixing is mandatory so that the coating is cross-linked throughout. In order to prevent the liquid coating from being absorbed by the porous rubber mat, the first coat has to be done with a pore sealer (PC 41-010). The next coat can be applied after 10 – 12 hours without using a tack primer beforehand. Consumption: approx. 2,6 – 2,8 kg/m² for thickness of 2 mm
- Certifications and Compliance
- ISO 14001
- ISO 45001
- ISO 50001
- ISO 9001
- Ready to Use Product Features
- Abrasion Resistant
- Good Adhesion
- Improved Flexibility
Technical data
Table 1 of 1
11 rows| Characteristic | Value | Unit |
|---|---|---|
| Density (at 23°C) (Part A) | 1,35 | g/cm³ |
| Hardness | 70 - 80 | Shore A |
| Density (at 23°C) (Part B) | 1,22 | g/cm³ |
| Viscosity (at 23°C) (Part A) | 2300 ± 700 | mPas |
| Viscosity (at 23°C) (Part B) | 400 ± 50 | mPas |
| Mixing Ratio (Part A : Part B (By Weight)) | 100 : 28 | — |
| Pot Life (at 23°C) | 45 ± 5 | Minutes |
| Drying Time (Accessible) | approx. 12 | Hours |
| Processing Temperature | min. 15 | °C |
| Tensile Strength | 6,6 ± 0,5 | mPa |
| Elongation At Tear | 140 ± 10 | % |