Induron Coatings AC 403S ACRYLIC ELASTOMERIC COATING
- Chemical Family
- Acrylics & Acrylates
Induron AC 403 Acrylic Elastomeric Coating is a 100% acrylic, water borne, high build elastomeric coating that fills and bridges minor hairline cracks. AC 403 is available in AC 403S Smooth and AC 403TX Texture. This flexible finish coat provides long-term protection against wind driven rain and alternate freezing and thawing. It has excellent resistance to long-term exposure to sun light and will allow moisture vapor to escape from the substrate. It will expand and contract allowing minor substrate movements even at temperatures below freezing.
Product families
- Other Paints & Coatings
Other characteristics
- Features
Freeze/Thaw Stability, Good Sunlight Resistance, Long Term Protection
- Product Type
- Elastomeric Coating, Waterborne Coating
- Elastomeric Coating
- Waterborne Coating
- Application Method
- Brush, Roller, Spray
- Compatible Substrates & Surfaces
- Aluminum, Brick, Masonry, Metal, Steel
- Usage
AC403 is an esthetically pleasing, durable coating system for new and existing poured and precast concrete, concrete block, brick, stucco and steel substrates. AC 403 Acrylic Elastomeric coating contains rust inhibitive pigmentation and is suitable for interior and exterior surfaces.
- Note
Lower temperature, higher film build, and/or poor ventilation will retard dry time.
- Limitations
Do not apply below 40°F (4°C). Keep from freezing. Surface must be clean and structurally sound, free of all contaminants such as release agents, oil, grease, algae, laitance, and chalk. Do not use below grade. Coverage must be pinhole free to achieve waterproofing.
- Safety Data
This product is formulated free of lead, chromates, mercury or other toxic pigments.
- Technology
- Ready-to-Use Products
- Application Methods
- Brush
- Roller
- Spray
- Ready to Use Product Features
- Freeze/Thaw Stability
- Good Sunlight Resistance
- Long Term Protection
- Compatible Substrates and Surfaces
- Aluminum
- Brick
- Masonry
- Metal
- Steel
Technical data
Table 1 of 3
5 rows| Characteristic | Value | Unit |
|---|---|---|
| Volume Solids | 45 - 47 | % |
| Solids (by Weight) | 60 - 62 | % |
| Weight | 11.4 - 11.8 | lbs/gallon |
| Volatile Organic Contents (Unthinned) | 0.6 (75) | lbs/gallon (grams/liter) |
| Volatile Organic Contents Thinned (10%) | 0.6 (75) | lbs/gallon (grams/liter) |
Table 2 of 3
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Elongation | 130.0 | % | ASTM D 412 |
| Moisture Vapor Permeability | 3.84 | Perms | ASTM E 96 |
| Exterior Durability (QUV, 500 Hour) | No Deterioration | — | ASTM D 4587 |
| Dry Time to Handle (50°F) | 12.0 | hours | — |
| Dry Time to Recoat (50°F) | 48.0 | hours | — |
| Coverage (Theoretical, at 1.0 mil dry film thickness, no loss) | 738.0 | sq. ft/gal | — |
| Dry Film Thickness | 4.0 - 12.0 | mils per coat. | — |
| Wet Film Thickness | 8.0 - 24.0 | mils per coat. | — |
| Dry Time to Handle (70°F) | 6.0 | hours | — |
| Dry Time to Handle (90°F) | 3.0 | hours | — |
| Dry Time to Recoat (70°F) | 24.0 | hours | — |
| Dry Time to Recoat (90°F) | 12.0 | hours | — |
Table 3 of 3
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Wind Driven Rain | Pass | 24 Hours | TT-C-555B |