International Chem-Crete Zinc Rich EP
- Chemical Family
- Epoxy & Epoxy Derivatives
ZINC RICH EP is an organic ZINC RICH Epoxy system recommended for use in the new construction and maintenance. ZINC RICH EP provides cathodic protection of reinforcement steel thus prevents the corrosion of construction rebars.
Product families
Ready-to-Use Products — Paints & Coatings
- Primers & Sealers
Other characteristics
- Features
Abrasion Resistant, Corrosion Resistant, High Performance, Wear Resistant
- Product Type
- 2K (2 component) Coating, Epoxy Coating, Primer
- 2K (2 component) Coating
- Epoxy Coating
- Primer
- Application Method
- Brush, Roller, Spray
- Compatible Substrates & Surfaces
- Metal, Steel
- Markets
- Paints & Coatings
- Printing & Packaging
- Storage
The product can be stored for minimum of twelve months at temperature from 50F to 95F (10C to 35C) in the unopened original packaging. Protect from direct sunlight and avoid sources of ignition.
- Cleaning
Remove uncured ZINC RICH EP from tools and equipment with suitable solvents such as Xylene, Toluene or CHEM CRETE BLENDED SOLVENT immediately after use. Cured material may only be removed mechanically.
- Technology
- Ready-to-Use Products
- Packaging Type
- Pails
- System Features
- Easily applied
- High performance anti-corrosion primer.
- Pulp Good chemical resistance
- Excellent wear and abrasion resistance
Technical data
Table 1 of 3
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Resin) | 14.77 | lb/gal | ASTM D-1475 |
| Mixing Ratio (Resin, by Volume) | approx. 2: 1 | — | — |
| Shelf Life (Resin) | 2 Year | — | — |
| Solids (Resin) | 71.25 | % | — |
Table 2 of 3
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Hardener) | 7.66 | lb/gal | ASTM D-1475 |
| Mixing Ratio (Hardener, by Volume) | approx. 2: 1 | — | — |
| Shelf Life (Hardener) | 2 Year | — | — |
| Solids (Hardener) | 44.1 | % | — |
Table 3 of 3
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Bond Strength to Steel (7 Days) | 96.0 | psi | ASTM C321 |
| Elongation | min. 30 | % | ASTM D-522, Method A |
| Final Cure | 7.0 | days | ASTM D570 |
| Gel Time (60 g) | min. 8 | hour | ASTM D-2471 |
| Hardness (3 Days) | 20.0 | Shore D | ASTM D-2240 |
| Mixed Density | 12.33 | lb/gal | ASTM D-1475 |
| Solid Content (by Weight) | 66.0 | % | — |
| Typical Thickness | 4 - 6 | mil | — |