Badamid® T70
- Chemical Family
- Polyamides
Properties
- Physical Form
- Granules
- Solid
Product families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- Badamid
- Polymer Name
- Polyamide 6/6T (PA 6/6T)
- Processing Methods
- Extrusion, Injection Molding
- Technology
- Plastics
- Material Features
- Good Toughness
- High Stiffness
- Low Water Absorption
- Country Availability
- Brazil
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- Halal
- Kosher
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
- Injection Molding
Technical data
Table 1 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 3200 / 3200 | MPa | ISO 527 |
| Yield stress | 100 / 90 | MPa | ISO 527 |
| Yield strain | 4.5 / 4.5 | % | ISO 527 |
| Nominal strain at break | 11.5 / 11.5 | % | ISO 527 |
| Charpy impact strength (+23°) | 100 / 100 | kJ/m2 | ISO 179/1eU |
| Charpy notched impact strength (+23°) | 12.0/10.0 | kJ/m2 | ISO 179/1eA |
| Izod notched impact strength, +23° | 7 / - | kJ/m2 | ISO 180/1A |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1160 / - | kg/m3 | ISO 1183 |
Table 3 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Linear Thermal Expansion (parallel) | 60 / * | E-6/K | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (normal) | 60 / * | E-6/K | ISO 11359-1/-2 |
| Temperature of deflection under load (1.80 Mpa) | 100 / * | °C | ISO 75-1/-2 |
| Temperature of deflection under load (0.45 Mpa) | 120 / * | °C | ISO 75-1/-2 |
| Melting temperature (10°C/min) | 295 / * | °C | ISO 11357-1/-3 |
Table 4 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity | 1E11 / 1E10 | ohm.m | IEC 60093 |
Table 5 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water absorption | 7 / * | % | Sim. to ISO 62 |
| Humidity absorption | 1.8 / * | % | Sim. to ISO 62 |