Badalac® ABS 20 GF15
- Chemical Family
- Acrylonitrile Butadiene Styrene (ABS)Styrenics
Properties
- Physical Form
- Granules
- Solid
Product families
Plastics — Basic Thermoplastics
- Styrenics
Other characteristics
- Brand
- Badalac
- Polymer Name
- Acrylonitrile Butadiene Styrene (ABS)
- Fillers Included
- Glass Fiber
- Processing Methods
- Injection Molding
- Flame Rating
- IEC 60695-11-10 HB
- Technology
- Plastics
- Country Availability
- Brazil
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Stress at break | 85 | MPa | ISO 527 |
| Tensile Modulus | 6000 | MPa | ISO 527-2/1A/1 |
| Strain at break | 2 | % | ISO 527 |
| Charpy notched impact strength (+23°) | 5 | kJ/m2 | ISO 179/1eA |
| Charpy impact strength (+23°) | 25 | kJ/m2 | ISO 179/1eU |
| Charpy notched impact strength (-30°) | 4 | kJ/m2 | ISO 179/1eA |
| Charpy impact strength (-30°) | 20 | kJ/m2 | ISO 179/1eU |
Table 2 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Volume Flow Rate - MVR (220°C/10 kg) | 10 | cm3/10 min | ISO 1133 |
| Density | 1100 | kg/m3 | ISO 1183 |
Table 3 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Temperature of deflection under load (0.45 Mpa) | 115 | °C | ISO 75-1/-2 |
| Temperature of deflection under load (1.80 Mpa) | 110 | °C | ISO 75-1/-2 |
| Thickness tested | 0.8 | mm | — |
| Vicat softening temperature | 116 | °C | ISO 306 |
| Burning Behavior at thickness | HB | class | IEC 60695-11-10 |
Table 4 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistivity | 1.00E+13 | ohm | IEC 60093 |
| Volume Resistivity | 100000000000.0 | ohm.m | IEC 60093 |
Table 5 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water absorption | 0.9 | % | Sim. to ISO 62 |
| Humidity absorption | 0.2 | % | Sim. to ISO 62 |