To catalogue
Badamid® A70 TM-Z3
- Chemical Family
- Polyamides
Properties
- Physical Form
- Granules
- Solid
Product families
Applications
Automotive & Transportation — Automotive
- Other Automotive Applications
Building & Construction — Building Materials
- Other Building Materials
- Structural Components
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
- Other Industrial Applications
Electrical & Electronics — Parts & Components
- Other Parts & Components
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- Badamid
- Polymer Name
- Polyamide 66 (PA 66)
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Building & Construction
- Electrical & Electronics
- Industrial
- Flame Rating
- IEC 60695-11-10 HB
- Technology
- Plastics
- Material Features
- Abrasion Resistant
- Good Thermal Stability
- High Rigidity
- Country Availability
- Brazil
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Construction Applications
- Machine/Mechanical Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus | 1900 / 950 | MPa | ISO 527 |
| Yield stress | 45 / 40 | MPa | ISO 527 |
| Yield strain | 5.7 / 22 | % | ISO 527 |
| Charpy impact strength (+23°) | N / N | kJ/m2 | ISO 179/1eU |
| Charpy impact strength (-30°) | N / - | kJ/m2 | ISO 179/1eU |
| Charpy notched impact strength (-30°) | 20 / - | kJ/m2 | ISO 179/1eA |
| Charpy notched impact strength (+23°) | 90 / 140 | kJ/m2 | ISO 179/1eA |
| Nominal Strain at Break (conditioned 23°C, 50 % R.F) | min. 50 | % | ISO 527 |
| Nominal Strain at Break (Dry as Molded) | 35 | % | ISO 527 |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1070 / - | kg/m3 | ISO 1183 |
Table 3 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Temperature of deflection under load (0.45 Mpa) | 130 / * | °C | ISO 75-1/-2 |
| Temperature of deflection under load (1.80 Mpa) | 60 / * | °C | ISO 75-1/-2 |
| Melting temperature (10°C/min) | 262 / * | °C | ISO 11357-1/-3 |
| Thickness tested | 0.8 / * | mm | — |
| Burning Behavior at 1.5 mm nominal thickness | HB / * | class | IEC 60695-11-10 |
| Burning Behavior at thickness | HB / * | class | IEC 60695-11-10 |
Table 4 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistivity | 1.00E+11 | ohm | IEC 60093 |
| Volume Resistivity | 1E13 / 1E10 | ohm.m | IEC 60093 |
Table 5 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Water absorption | 6.5 / * | % | Sim. to ISO 62 |
| Humidity absorption | 2.1 / * | % | Sim. to ISO 62 |