WIC PA6 30 N
- Chemical Family
- Polyamides
WIC PA6 30 N is a heat-aging stabilized polyamide 6 base polymer filled with 30% carbon fiber and is natural (carbon optic) in color. It is suitable for injection molding, with a melt temperature of 250-270°C and a mold temperature of 60-100°C. Pre-drying conditions require the material to be dried in an air circulating dryer for 2-8 hours at 80°C, depending on the moisture content, with a maximum moisture content of 0.12%. Additionally, under certain conditions, the increased thermal conductivity should be taken into consideration. This material is used in the automotive and sport markets.
Product families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- WIC
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Carbon Fiber
- Processing Methods
- Injection Molding
- Color
- Natural
- Markets
- Consumer Goods
- Applications
- Consumer Goods — Sports & Recreation
- Technology
- Plastics
- Labeling Claims
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Heat Aging Resistant
- Medium Viscosity
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 80°C in an air circulating dryer for 2-8h
- Dependant on moisture content
- Certifications and Compliance
- IATF 16949
- ISO 13485
- ISO 14001
- ISO 17025
- ISO 45001
- ISO 50001
- ISO 9001
- RoHS Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Sporting Goods
- Plastics and Elastomers Functions
- Resin
- Injection Moulding Processing Conditions
Under certain conditions the increased thermal conductivity must be considered.
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 20000.0 | MPa | ISO 178 |
| Flexural Modulus (Conditioned) | 11500.0 | MPa | ISO 178 |
| Flexural Strength (Dry) | 290.0 | MPa | ISO 178 |
| Flexural Strength (Conditioned) | 200.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 22500.0 | MPa | ISO 527 |
| Tensile Modulus (Conditioned) | 11500.0 | MPa | ISO 527 |
| Tensile Strength (Dry) | 200.0 | MPa | ISO 527 |
| Tensile Strength (Conditioned) | 125.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 1.5 | % | ISO 527 |
| Tensile Elongation at Break (Conditioned) | 3.2 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 55.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Conditioned, Charpy, at 23°C) | 65.0 | kJ/m² | ISO 179/1eU |
Table 2 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1270.0 | kg/m³ | ISO 1183 |
| Global Warming Potential (GWP) | 5.23 | kg CO₂ eq. | ISO 14040, 14044 |
Table 3 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 (Dry) | 215.0 | °C | ISO 306 |
| HDT / A (Dry, 1.8 MPa) | 215.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 220.0 | °C | ISO 11357-1/-3 |
| Coeffecient of Linear Thermal Expansion (parallel, dry) | 6.7 | E⁻⁶/K | ISO 11359-1/-2 |
| Coeffecient of Linear Thermal Expansion (normal, dry) | 103.0 | E⁻⁶/K | ISO 11359-1/-2 |
Table 4 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.12 | % |
Table 5 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistance (Conditioned) | max. 10 | Ohm | IEC 62631-3-2 |
| Specific Volume Resistance (Dry) | 0.1 | Ohm*m | IEC 62631-3-1 |
Table 6 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 250 - 270 | °C |
| Mould Temperature | 60 - 100 | °C |
Table 7 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR, Dry) | 30.0 | cm³/10min | ISO 1133 |
| MVR Temperature (Dry) | 275.0 | °C | — |
| MVR Load (Dry) | 5.0 | kg | — |
| Molding Shrinkage (parallel, Dry) | 0.1 | % | ISO 294-4, 2577 |
| Molding Shrinkage (normal, Dry) | 0.4 | % | ISO 294-4, 2577 |