ALCOM® PA66 910/1 PTFE10
- Chemical Family
- Polyamides
MOCOM Compounds ALCOM® PA66 910/1 PTFE10 is a polyamide 66 base polymer with a 10% PTFE filler/additive system, improved for sliding/wear and heat stability, designed for the automotive and machinery markets. It is typically used for injection molded functional components, bearings, and sliding elements. The processing injection molding melt temperature should be between 280-300°C and the mold temperature should be between 80-120°C. No extra sentence is needed.
Product families
- Polyamides
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- PTFE
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Good Sliding Properties
- Heat Stabilized
- Improved Wear
- Wear Resistant
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer <80 °C for 2-12 h; Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Bearings
- Machine/Mechanical Parts
- Sliding Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 2800.0 | MPa | ISO 178 |
| Flexural Stress (Dry, 3.5% Strain) | 90.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 3200.0 | MPa | ISO 527 |
| Tensile Strength at Break (Dry) | 75.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 5.8 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 75.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Dry, Charpy, at -40°C) | 60.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Dry, Charpy, at 23°C) | 3.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Dry, Charpy, at -40°C) | 3.0 | kJ/m² | ISO 179/1eA |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1200.0 | kg/m³ | ISO 1183 |
Table 3 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 80.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 263.0 | °C | ISO 11357 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 280 - 300 | °C |
| Mould Temperature | 80 - 120 | °C |
Table 5 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 1.6 - 2 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 1.8 - 2.2 | % | ISO 294-4 |