ALTECH® PA66 A 2020/109 GF20
- Chemical Family
- Polyamides
MOCOM Compounds ALTECH® PA66 A 2020/109 GF20 is a heat-stabilized polyamide 66 with a 20% glass fiber filler/additive system. It is suitable for injection molding with a melt temperature range of 280-300°C and a mold temperature range of 80-120°C. It is well-suited for a variety of injection molded parts in the automotive industry, such as clips and interior decoration/finishing. It is also designed with easy release (demolding) and slip agent features for optimal performance. To ensure best results, it should be stored dry and protected from light at a temperature not exceeding 30°C.
Product families
Applications
- Interior
Product Families
- Polyamides
Other characteristics
- Brand
- ALTECH
- End Uses
Automotive Applications, Automotive Interior Parts, Clips
- Features
- Good Mold Release, Heat Stabilized
- Functions
- Resin
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Fiber
- Additives Included
- Heat Stabilizer, Slip Agent
- Heat Stabilizer
- Slip Agent
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Good Mold Release
- Heat Stabilized
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Interior Parts
- Clips
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 6200.0 | MPa | ISO 178 |
| Flexural Strength (Dry) | 220.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 6800.0 | MPa | ISO 527 |
| Tensile Strength at Break (Dry) | 140.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 2.7 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 35.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Dry, Charpy, at 23°C) | 6.0 | kJ/m² | ISO 179/1eA |
Table 2 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1290.0 | kg/m³ | ISO 1183 |
Table 3 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 250.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 263.0 | °C | ISO 11357 |
Table 4 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.15 | % |
Table 5 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (Dry, 0.75 mm) | HB | class | UL 94 |
| UL Recognition (Dry) | yes | — | — |
Table 6 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 280 - 300 | °C |
| Mould Temperature | 80 - 120 | °C |
Table 7 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 0.3 - 0.5 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.9 - 1.1 | % | ISO 294-4 |