ALTECH® PA66 A 2030/109 GF30 GY1176-12LS
- Chemical Family
- Polyamides
MOCOM Compounds ALTECH® PA66 A 2030/109 GF30 GY1176-12LS is a polyamide 66-based injection molding grade material that contains 30% glass fibers as filler. It has a heat-stabilized formulation, which ensures good dimensional stability and resistance to high temperatures during processing and end-use. The material is easy to release from the mold due to its easy-release (demolding) properties. It also has good flowability and is laser-etchable, making it ideal for applications where markings or logos need to be etched onto the surface.
Product families
Applications
- Housings & Enclosures
Product Families
- Polyamides
Other characteristics
- Brand
- ALTECH
- End Uses
- Housings
- Features
Good Flow, Good Mold Release, Heat Stabilized, Laser Etchable, Laser Markable
- Functions
- Resin
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Fiber
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Markets
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Good Flow
- Good Mold Release
- Heat Stabilized
- Laser Etchable
- Laser Markable
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Housings
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 8500.0 | MPa | ISO 178 |
| Flexural Strength (Dry) | 245.0 | MPa | ISO 178 |
| Flexural Strength (Conditioned) | 180.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 9700.0 | MPa | ISO 527 |
| Tensile Modulus (Conditioned) | 7250.0 | MPa | ISO 527 |
| Tensile Strength at Break (Dry) | 160.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 2.7 | % | ISO 527 |
| Tensile Strength at Break (Conditioned) | 100.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Conditioned) | 4.0 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 50.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Dry, Charpy, at 23°C) | 7.0 | kJ/m² | ISO 179/1eA |
Table 2 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1360.0 | kg/m³ | ISO 1183 |
Table 3 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 250.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 263.0 | °C | ISO 11357 |
Table 4 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.15 | % |
Table 5 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (Dry, 0.75 mm) | HB | class | UL 94 |
| UL Recognition (Dry) | yes | — | — |
Table 6 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 280 - 300 | °C |
| Mould Temperature | 80 - 120 | °C |
Table 7 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 0.2 - 0.4 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.7 - 0.9 | % | ISO 294-4 |