ALTECH® PA66 A 2040/100.01 GF40
- CAS Number
- 9002-93-1
- Chemical Family
- Polyamides
MOCOM Compounds ALTECH® PA66 A 2040/100.01 GF40 is a polyamide 66 filled with 40% glass fibers that is heat stabilized and suitable for injection molding. It provides an improved surface appearance and high stiffness, making it ideal for automotive and machinery parts such as pedals and highly stressed components. Pre-drying conditions should be 80°C in a dry air (dessiccant) dryer for 2-12 hours, depending on the moisture content, with the maximum moisture content of 0.15%. The melt temperature should be between 280-300°C and the mold temperature should be 80-120°C.
Product families
Applications
- Interior
Product Families
- Polyamides
Other characteristics
- Brand
- ALTECH
- Functions
- Resin
- Polymer Name
- Polyamide 66 (PA 66)
- Labeling Claims
Azo Colorants-free, Azo Dyes-free, Conflict minerals-free, PAH-free, PFOA-free, PFOS-free, Persistent Organic Pollutants (POP)-free; Azo Colorants-free; Azo Dyes-free; Conflict minerals-free; PAH-free; PFOA-free; PFOS-free; Persistent Organic Pollutants (POP)-free
- Fillers Included
- Glass Fiber
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Technology
- Plastics
- Material Features
- Good Surface Appearance
- Heat Stabilized
- High Stiffness
- Storage Condition
Store in dry, tighlty sealed protected from light not above 30°C.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Interior Parts
- Machine/Mechanical Parts
- Pedal
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 12000.0 | MPa | ISO 178 |
| Flexural Modulus (Conditioned) | 7700.0 | MPa | ISO 178 |
| Flexural Strength (Dry) | 310.0 | MPa | ISO 178 |
| Flexural Strength (Conditioned) | 215.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 13000.0 | MPa | ISO 527 |
| Tensile Modulus (Conditioned) | 8400.0 | MPa | ISO 527 |
| Tensile Strength at Break (Dry) | 205.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 3.0 | % | ISO 527 |
| Tensile Strength at Break (Conditioned) | 135.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Conditioned) | 5.0 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 90.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Conditioned, Charpy, at 23°C) | 100.0 | kJ/m² | ISO 179/1eU |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1450.0 | kg/m³ | ISO 1183 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 255.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 263.0 | °C | ISO 11357 |
Table 4 of 6
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.15 | % |
Table 5 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 280 - 300 | °C |
| Mould Temperature | 80 - 120 | °C |
Table 6 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 0.1 - 0.3 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.6 - 0.8 | % | ISO 294-4 |