ALTECH® IQ PA6.6 2050/W100 BK0002
- Chemical Family
- Polyamides
MOCOM Compounds ALTECH® IQ PA6.6 2050/W100 BK0002 is a polyamide 66-based polymer with 50% glass fiber filler, black in color and of industrial quality. It has a maximum moisture content of 0.12% and requires pre-drying conditions with an 80°C air circulating dryer for 2-8h, depending on the moisture content. The processing conditions call for an injection molding melt temperature of 280-300°C and a mold temperature of 80-120°C. This product is used in various market segments and should be stored in a dry, light-protected place.
Product families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- ALTECH® IQ
- Synonyms
- Methylsulfonic Acid
- Functions
- Resin
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Fiber
- Processing Methods
- Injection Molding
- Color
- Black
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 80°C in an air circulating dryer for 2-8h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
18 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 11500.0 | MPa | ISO 178 |
| Flexural Modulus (Conditioned) | 7500.0 | MPa | ISO 178 |
| Flexural Strength (Dry) | 240.0 | MPa | ISO 178 |
| Flexural Strength (Conditioned) | 150.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 12500.0 | MPa | ISO 527 |
| Tensile Modulus (Conditioned) | 8000.0 | MPa | ISO 527 |
| Tensile Strength (Dry) | 140.0 | MPa | ISO 527 |
| Tensile Strength (Conditioned) | 100.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 3.0 | % | ISO 527 |
| Tensile Elongation at Break (Conditioned) | 5.2 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 54.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Conditioned, Charpy, at 23°C) | 59.0 | kJ/m² | ISO 179/1eU |
Table 2 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1550.0 | kg/m³ | ISO 1183 |
| Humidity Absorption (Dry) | 0.2 | % | Sim. to ISO 62 |
| Water Absorption (Dry) | 2.2 | % | Sim. to ISO 62 |
| Global Warming Potential (GWP) | 0.84 | kg CO₂ eq. | ISO 14040, 14044 |
Table 3 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| DSC (Melt Point, Dry) | 265.0 | °C | ISO 11357-1/-3 |
Table 4 of 6
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.12 | % |
Table 5 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 280 - 300 | °C |
| Mould Temperature | 80 - 120 | °C |
Table 6 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR, Dry) | 20.0 | cm³/10min | ISO 1133 |
| MVR Temperature (Dry) | 300.0 | °C | — |
| MVR Load (Dry) | 1.2 | kg | — |
| Molding Shrinkage (parallel, Dry) | 0.3 | % | ISO 294-4, 2577 |
| Molding Shrinkage (normal, Dry) | 0.7 | % | ISO 294-4, 2577 |