ALTECH® PA6 TG 2015/717 GF15

Chemical Family: Polyamides

MOCOM Compounds ALTECH® PA6 TG 2015/717 GF15 is a polyamide 6 with 15% glass fibers that is heat-stabilized and elastomer-modified for easy demolding and high toughness. It has many automotive applications, including injection-molded housings, cable guides, and other parts. To prepare, pre-dry at 80°C in a dry air (desiccant) dryer for 2-12 hours, depending on moisture content, and ensure a maximum moisture content of <0.15%. For processing, the melt temperature should be between 270-290°C, and the mold temperature should be between 80-100°C.

Product families

Applications

Electrical & Electronics — Parts & Components

Housings & Enclosures

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: ALTECH
Functions: Resin
Polymer Name: Polyamide 6 (PA 6)
Labeling Claims: Azo Colorants-free, Azo Dyes-free, Conflict minerals-free, PAH-free, PFOA-free, PFOS-free, Persistent Organic Pollutants (POP)-free; Azo Colorants-free; Azo Dyes-free; Conflict minerals-free; PAH-free; PFOA-free; PFOS-free; Persistent Organic Pollutants (POP)-free
Fillers Included: Glass Fiber
Additives Included: Heat Stabilizer
Processing Methods: Injection Molding
Markets: Electrical & Electronics
Technology: Plastics
Material Features: Elastomer Modified
Excellent Toughness
Good Mold Release
Heat Stabilized
Storage Condition: Store in dry, protected from light not above 30°C.
Pre-Drying Conditions: 80 °C in a dry air (dessiccant) dryer for 2-12 h
Dependant on moisture content
Certifications and Compliance: Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
Plastics and Elastomers End Uses: Automotive Applications
Cable Guides
Housings
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 6

7 rows

Characteristic	Value	Unit	Method
Flexural Modulus (Dry)	4500.0	MPa	ISO 178
Flexural Strength (Dry)	150.0	MPa	ISO 178
Tensile Modulus (Dry)	5100.0	MPa	ISO 527
Tensile Strength at Break (Dry)	90.0	MPa	ISO 527
Tensile Elongation at Break (Dry)	3.8	%	ISO 527
Impact Strength (Dry, Charpy, at 23°C)	60.0	kJ/m²	ISO 179/1eU
Notched Impact Strength (Dry, Charpy, at 23°C)	13.0	kJ/m²	ISO 179/1eA

Table 2 of 6

1 row

Characteristic	Value	Unit	Method
Density (Dry)	1190.0	kg/m³	ISO 1183

Table 3 of 6

3 rows

Characteristic	Value	Unit	Method
Vicat B50 (Dry)	202.0	°C	ISO 306
HDT / A (Dry, 1.8 MPa)	184.0	°C	ISO 75-1/-2
DSC (Melt Point, Dry)	220.0	°C	ISO 11357