ALCOM® CFX ABS 1000 UV 16002 GY1001-16MCS

Chemical Family: Acrylonitrile Butadiene Styrene (ABS)Styrenics

MOCOM Compounds ALCOM® CFX ABS 1000 UV 16002 GY1001-16MCS is a UV stabilized Acrylonitrile/Butadiene/Styrene/Copolymer with a metallic effect. It is suitable for injection molded housings and should be pre-dried by 80°C in a dry air (dessiccant) dryer for 2-4 hours, or 80°C in an air circulating dryer for 3-6 hours depending on moisture content. The melt temperature for processing should be between 220-260°C and the mold temperature should be between 50-80°C. Additionally, it should be stored in a dry, light-protected environment.

Product families

Applications

Electrical & Electronics — Parts & Components

Housings & Enclosures

Product Families

Plastics — Basic Thermoplastics

Styrenics

Other characteristics

Brand: ALCOM
Polymer Name: Acrylonitrile Butadiene Styrene (ABS)
Additives Included: UV Stabilizer
Processing Methods: Injection Molding
Markets: Electrical & Electronics
Technology: Plastics
Labeling Claims: Azo Colorants-free
Azo Dyes-free
Conflict minerals-free
PAH-free
PFOA-free
PFOS-free
Persistent Organic Pollutants (POP)-free
Material Features: UV Stabilized
Storage Condition: Store in dry, protected from light.
Pre-Drying Conditions: 80 °C in a dry air (dessiccant) dryer for 2-4 h
80 °C in an air circulating dryer for 3-6 h
Dependant on moisture content
Certifications and Compliance: Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
Plastics and Elastomers End Uses: Housings
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

11 rows

Characteristic	Value	Unit	Method
Flexural Modulus	2800.0	MPa	ISO 178
Flexural Stress (3.5% Strain)	75.0	MPa	ISO 178
Tensile Modulus	2600.0	MPa	ISO 527
Tensile Stress at Yield	48.0	MPa	ISO 527
Tensile Elongation at Yield	2.7	%	ISO 527
Tensile Elongation at Break	22.0	%	ISO 527
Impact Strength (Charpy, at 23°C)	75.0	kJ/m²	ISO 179/1eU
Impact Strength (Charpy, at -40°C)	60.0	kJ/m²	ISO 179/1eU
Notched Impact Strength (Charpy, at 23°C)	11.0	kJ/m²	ISO 179/1eA
Notched Impact (Charpy, at -40°C)	4.0	kJ/m²	ISO 179/1eA
Ball Indentation Hardness (H358/30)	100.0	MPa	ISO 2039-1

Table 2 of 5

1 row

Characteristic	Value	Unit	Method
Density	1060.0	kg/m³	ISO 1183

Table 3 of 5

2 rows

Characteristic	Value	Unit	Method
Vicat B50	104.0	°C	ISO 306
HDT / A (1.8 MPa)	89.0	°C	ISO 75-1/-2

Table 4 of 5