WIPAFLEX TV 10 BK
WIPAFLEX TV 10 BK is a black material with heat-age stabilization properties intended for use in various automotive applications. The material is a blend of polypropylene, polyethylene, and EPDM, with 10% talc added as a filler. Prior to processing via injection molding, the material must be pre-dried at temperatures between 60 and 100°C for 2-4 hours, depending on its moisture content, which should not exceed 0.10%. During injection molding, the material should be melted at temperatures ranging from 200 to 270°C, with a mold temperature between 20 and 60°C. All temperatures must be carefully monitored to ensure they fall within the specified ranges.
Product families
Elastomers — Thermoplastic Elastomers
- Thermoplastic Olefin Elastomers (TPO)
Other characteristics
- Brand
- WIPAFLEX
- Density
- 980.0 - 980.0 kg/m³
- Features
- Heat Aging Resistant
- Polymer Name
- PP/PE/EPDM
- Strain at Break
- 40.0 - 40.0 %
- Flexural Modulus
- 1000.0 - 1000.0 MPa
- Processing Methods
- Injection Molding
- Color
- Black
- Technology
- Elastomers
- Labeling Claims
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Fillers Included
- Talc
- Material Features
- Heat Aging Resistant
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 60-100°C in an air circulating dryer for 2-4h
- Dependant on moisture content
- Certifications and Compliance
- IATF 16949
- ISO 13485
- ISO 14001
- ISO 17025
- ISO 45001
- ISO 50001
- ISO 9001
- RoHS Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 1000.0 | MPa | ISO 178 |
| Flexural Strength | 20.0 | MPa | ISO 178 |
| Shore Hardness D (15s) | 60.0 | — | ISO 868 |
| Tensile Modulus | 1200.0 | MPa | ISO 527 |
| Tensile Strength | 15.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 40.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 95.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 31.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 25.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 2.5 | kJ/m² | ISO 179/1eA |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 980.0 | kg/m³ | ISO 1183 |
Table 3 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 54.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 56.0 | °C | ISO 75-1/-2 |
| HDT / B (0.45 MPa) | 88.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 163.0 | °C | ISO 11357-1/-3 |
Table 4 of 6
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.1 | % |
Table 5 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Mould Temperature | 20 - 60 | °C |
| Melt Temperature | 200 - 270 | °C |
Table 6 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 13.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 230.0 | °C | — |
| MVR Load | 2.16 | kg | — |
| Molding Shrinkage (parallel) | 1.0 | % | ISO 294-4, 2577 |
| Molding Shrinkage (normal) | 1.1 | % | ISO 294-4, 2577 |