ALCOM® AWL 109/15 UV WT1217-11LB
MOCOM Compounds ALCOM® AWL 109/15 UV WT1217-11LB is a base polymer of acrylonitrile/butadiene/styrene/copolymer modified with polycarbonate, containing 15% special filler and special features of being highly reflective, opaque, UV stabilized, and highly heat stabilized. It is intended for use in the automotive and various market segments, primarily for lighting and light blocking components such as light guides and reflectors.
Product families
Applications
Automotive & Transportation — Automotive
- Aftermarket Parts & Components
- Automotive Lighting
- Exterior & Body
Product Families
Plastics — Engineering & Specialty Polymers
- Blends & Alloys
Other characteristics
- Brand
- ALCOM
- Density
- 1240.0 - 1240.0 kg/m³
- Polymer Name
- PC/ABS Alloy
- Flexural Modulus
- 2700.0 - 2700.0 MPa
- Processing Methods
- Injection Molding
- Color
- White
- Markets
- Automotive & Transportation
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Fillers Included
- Mineral
- Proprietary
- Additives Included
- Heat Stabilizer
- UV Stabilizer
- Material Features
- Excellent Opacity
- Good Light Reflection
- Heat Stabilized
- High Reflectivity
- Light Blocking
- UV Resistant
- UV Stabilized
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 80-90 °C for 2-4 h; In an air circulatIng dryer 80-90 °C for 4-8 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Exterior Parts
- Control Panel
- LED Housing
- Light Blocking Components
- Light Guides
- Reflectors
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 8
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2700.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 75.0 | MPa | ISO 178 |
| Tensile Modulus | 2700.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 50.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 3.0 | % | ISO 527 |
| Tensile Elongation at Break | 13.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 80.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 13.0 | kJ/m² | ISO 179/1eA |
| Ball Indentation Hardness (H358/30) | 115.0 | MPa | ISO 2039-1 |
Table 2 of 8
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1240.0 | kg/m³ | ISO 1183 |
Table 3 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 110.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 100.0 | °C | ISO 75-1/-2 |
Table 4 of 8
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.02 | % |
Table 5 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tristimulus Value Y10 of Reflection | 92.0 | % | DIN 5033 |
| Tristimulus Value Y10 of Transm.,d=0.5mm | 0.4 | % | ISO 13468 |
Table 6 of 8
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (1.5 mm) | HB | class | UL 94 |
| Flammability (3.0 mm) | HB | class | UL 94 |
| Fire Behavior FMVSS (2.0 mm) | Passed | — | FMVSS 302/DIN 75200 |
Table 7 of 8
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 230 - 270 | °C |
| Mould Temperature | 60 - 100 | °C |
Table 8 of 8
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 15.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 220.0 | °C | — |
| MVR Load | 10.0 | kg | — |