ALCOM® PBT 700/9 BK2034-06MCS
- Chemical Family
- Polyesters
MOCOM Compounds ALCOM® PBT 700/9 BK2034-06MCS is a polybutylene terephthalate base polymer with a matt (textured) surface, used in building and construction, fixtures/fittings, household goods, and kitchenware for various applications. For optimal results, it should be pre-dried in a dry air (dessiccant) dryer at 100-120°C for 2-4 hours or in an air circulating dryer at 100-120°C for 4-8 hours, depending on moisture content. During processing, injection molding should be used with a melt temperature of 250-270°C and a mold temperature of 60-100°C. To ensure maximum product quality, the product should be protected from light at temperatures not exceeding 30°C.
Product families
Applications
- Consumer Goods — Housewares
- Pipes & Plumbing
Product Families
- Polyesters & Copolyesters
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polybutylene Terephthalate (PBT)
- Flexural Modulus
- 2700.0 - 2700.0 MPa
- Processing Methods
- Injection Molding
- Markets
- Building & Construction
- Consumer Goods
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Matte Finish
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 100-120 °C for 2-4 h; In an air circulatIng dryer 100-120 °C for 4-8 h; Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Construction Applications
- Fittings
- Fixtures
- Household Goods
- Kitchenware
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2700.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 80.0 | MPa | ISO 178 |
| Tensile Modulus | 2600.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 55.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 3.4 | % | ISO 527 |
| Tensile Elongation at Break | 12.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 67.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 40.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 3.5 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 3.0 | kJ/m² | ISO 179/1eA |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1320.0 | kg/m³ | ISO 1183 |
Table 3 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 178.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 61.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 226.0 | °C | ISO 11357 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 250 - 270 | °C |
| Mould Temperature | 60 - 100 | °C |
Table 5 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 11.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 250.0 | °C | — |
| MVR Load | 2.16 | kg | — |
| Shrinkage (Lengthwise, 24h) | 2 - 2.4 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 2 - 2.4 | % | ISO 294-4 |