ALTECH® PBT+ASA A 2020/510 GF20
MOCOM Compounds ALTECH® PBT+ASA A 2020/510 GF20 is an impact-modified, low-warpage, easy-flow polybutylene terephthalate + acrylonitrile styrene acrylate with a glass fiber filler/additive system. Pre-drying conditions require a dry air (desiccant) dryer at 80-120°C for 2-4 hrs depending on moisture content, with a maximum moisture content of <0.04%. Processing temperature for injection molding is 250-270°C and 60-100°C for the mold temperature. Typical applications include interior decoration/finishing, clothing/fasteners, and various other applications. It is ideal for applications requiring high mechanical strength, chemical resistance and heat stability.
Product families
Applications
- Textile Manufacturing
Product Families
- Blends & Alloys
Other characteristics
- Brand
- ALTECH
- Density
- 1410.0 - 1410.0 kg/m³
- Functions
- Resin
- Polymer Name
- PBT/ASA Alloy
- Labeling Claims
Azo Colorants-free, Azo Dyes-free, Conflict minerals-free, PAH-free, PFOA-free, PFOS-free, Persistent Organic Pollutants (POP)-free; Azo Colorants-free; Azo Dyes-free; Conflict minerals-free; PAH-free; PFOA-free; PFOS-free; Persistent Organic Pollutants (POP)-free
- Flexural Modulus
- 5960.0 - 5960.0 MPa
- Tensile Strength
- 95.0 - 95.0 MPa
- Processing Methods
- Injection Molding
- Markets
- Industrial
- Technology
- Plastics
- Fillers Included
- Glass Fiber
- Additives Included
- Impact Modifier
- Material Features
- Good Flow
- Impact Modified
- Low Warpage
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 80-120 °C for 2-4 h; Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Fasteners
- Textile Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 5960.0 | MPa | ISO 178 |
| Flexural Strength | 150.0 | MPa | ISO 178 |
| Tensile Modulus | 6850.0 | MPa | ISO 527 |
| Tensile Strength | 95.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 2.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 50.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 40.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 5.0 | kJ/m² | ISO 179/1eA |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1410.0 | kg/m³ | ISO 1183 |
Table 3 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 195.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 198.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 226.0 | °C | ISO 11357 |
Table 4 of 6
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.04 | % |
Table 5 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 250 - 270 | °C |
| Mould Temperature | 60 - 100 | °C |
Table 6 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 20.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 275.0 | °C | — |
| MVR Load | 2.16 | kg | — |
| Shrinkage (Lengthwise, 24h) | 0.2 - 0.6 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.5 - 1 | % | ISO 294-4 |