ALCOM® HP PBT 5262 18051
- Chemical Family
- Polyesters
MOCOM Compounds ALCOM® HP PBT 5262 18051 is a high-density, heat-stabilized, and high-acoustic damping polybutylene terephthalate with a 62% glass fiber/mineral filler/additive system. It is used for injection-molded parts in the automotive market, such as housings and functional components, with a melt temperature of 270-290°C and a mold temperature of 80-120°C. To ensure optimal performance, it should be stored in a dry place, protected from light.
Product families
Applications
Electrical & Electronics — Parts & Components
- Housings & Enclosures
Product Families
Plastics — Engineering & Specialty Polymers
- Polyesters & Copolyesters
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polybutylene Terephthalate (PBT)
- Fillers Included
- Glass/Mineral, Iron, Metal
- Glass/Mineral
- Iron
- Metal
- Flexural Modulus
- 12800.0 - 12800.0 MPa
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Markets
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Heat Stabilized
- High Density
- Noise Damping
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer <120 °C for 2-4 h; Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Housings
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 12800.0 | MPa | ISO 178 |
| Flexural Strength | 145.0 | MPa | ISO 178 |
| Tensile Modulus | 14500.0 | MPa | ISO 527 |
| Tensile Strength at Break | 100.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 1.2 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 28.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 25.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 4.5 | kJ/m² | ISO 179/1eA |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 2120.0 | kg/m³ | ISO 1183 |
Table 3 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 213.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 207.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 222.0 | °C | ISO 11357 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 270 - 290 | °C |
| Mould Temperature | 80 - 120 | °C |
Table 5 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 2.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 260.0 | °C | — |
| MVR Load | 2.16 | kg | — |
| Shrinkage (Lengthwise, 24h) | 0.2 - 0.4 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.4 - 0.6 | % | ISO 294-4 |