Alcom® PWL 10/1 WT 41-913LB
- Chemical Family
- Polycarbonate (PC)
MOCOM Compounds Alcom® PWL 10/1 WT 41-913LB is an impact-modified polycarbonate designed for use in automotive and lighting applications. It contains 15% special filler that gives it a highly reflective, opaque appearance, making it ideal for light blocking components. It should be stored in a dry area and protected from light.
Product families
Applications
Automotive & Transportation — Automotive
- Aftermarket Parts & Components
- Automotive Lighting
- Exterior & Body
Product Families
Plastics — Engineering & Specialty Polymers
- Polycarbonates
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polycarbonate (PC)
- Fillers Included
- Mineral, Proprietary
- Mineral
- Proprietary
- Flexural Modulus
- 2600.0 - 2600.0 MPa
- Additives Included
- Impact Modifier
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Excellent Opacity
- Good Light Reflection
- High Reflectivity
- Impact Modified
- Light Blocking
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
- 120 °C in a dry air (dessiccant) dryer for 2-4 h
- 120 °C in an air circulating dryer for 4-12 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Exterior Parts
- Light Blocking Components
- Light Guides
- Reflectors
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 8
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1300.0 | kg/m³ | ISO 1183 |
Table 2 of 8
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2600.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 75.0 | MPa | ISO 178 |
| Impact Strength (Charpy, at 23°C) | no break | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 38.0 | kJ/m² | ISO 179/1eA |
| Tensile Elongation at Break | 50.0 | % | ISO 527 |
| Tensile Elongation at Yield | 5.3 | % | ISO 527 |
| Tensile Modulus | 2600.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 56.0 | MPa | ISO 527 |
Table 3 of 8
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.02 | % |
Table 4 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (1.8 MPa) | 126.0 | °C | ISO 75-1/-2 |
| Vicat B50 | 142.0 | °C | ISO 306 |
Table 5 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tristimulus Value Y10 of Reflection | 97.0 | % | DIN 5033 |
| Tristimulus Value Y10 of Transm.,d=0.5mm | 1.4 | % | ISO 13468 |
Table 6 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (0.75 m) | HB | class | UL 94 |
| UL Recognition | yes | — | — |
Table 7 of 8
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 280 - 320 | °C |
| Mould Temperature | 80 - 110 | °C |
Table 8 of 8
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 8.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 300.0 | °C | — |
| MVR Load | 1.2 | kg | — |
| Shrinkage (24h) | 0.6 - 0.9 | % | ISO 294-4 |