TEDUR® L 9107-1 S

Chemical Family: Polyphenylene Sulfide (PPS)

MOCOM Compounds TEDUR® L 9107-1 S is a polyphenylene sulfide polymer containing 40% glass fibers designed for injection molding applications. It offers high toughness and reduced flash, with increased burst strength, making it suitable for the machinery market segment. Typical applications include pump impellers. The pre-drying conditions require the material to be placed in a dry air (dessiccant) dryer at a temperature of 130-140°C for 2-4 hours, depending on moisture content. For injection molding, a melt temperature of 320-340°C and mold temperature of greater than 140°C is required.

Product families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics

Other characteristics

Brand: TEDUR
Polymer Name: Polyphenylene Sulfide (PPS)
Fillers Included: Glass Fiber
Flexural Modulus: 14000.0 - 14000.0 MPa
Processing Methods: Injection Molding
Technology: Plastics
Labeling Claims: Azo Colorants-free
Azo Dyes-free
Conflict minerals-free
PAH-free
PFOA-free
PFOS-free
Persistent Organic Pollutants (POP)-free
Material Features: Excellent Toughness
Good Flow
High Temperature Resistance
Increased Burst Strength
Low Flash
Storage Condition: Store in dry, protected from light not above 30°C.
Pre-Drying Conditions: In a dry air (dessiccant) dryer 130-140 °C for 2-4 h; Dependant on moisture content
Certifications and Compliance: Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
Plastics and Elastomers End Uses: Machine/Mechanical Parts
Pump Impeller
Pump Parts
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 6

7 rows

Characteristic	Value	Unit	Method
Flexural Modulus	14000.0	MPa	ISO 178
Flexural Strength	300.0	MPa	ISO 178
Tensile Modulus	15200.0	MPa	ISO 527
Flexural Deflection (Maximum Force)	2.4	%	ISO 178
Tensile Strength at Break	195.0	MPa	ISO 527
Tensile Elongation at Break	1.8	%	ISO 527
Impact Strength (Charpy, at 23°C)	50.0	kJ/m²	ISO 179/1eU

Table 2 of 6

1 row

Characteristic	Value	Unit	Method
Density	1650.0	kg/m³	ISO 1183

Table 3 of 6

2 rows

Characteristic	Value	Unit	Method
HDT / A (1.8 MPa)	274.0	°C	ISO 75-1/-2
DSC (Melt Point)	280.0	°C	ISO 11357

Table 4 of 6