ALTECH® PP-H FC 2020/100.01
- Chemical Family
- PolyolefinsPolypropylenes (PP)
MOCOM Compounds ALTECH® PP-H FC 2020/100.01 is a polypropylene homopolymer reinforced with 20% glass fibers. It is suitable for injection molding at a melt temperature of 200-250°C and a mold temperature of 20-70°C, with features such as easy release (demolding), processing stability, and heat stability. This product is suitable for building and construction, packaging, food contact, household goods, thin walled parts, and kitchenware applications.
Product families
Applications
- Consumer Goods — Housewares
- Food & Beverage Packaging
Product Families
- Polyolefins
Other characteristics
- Brand
- ALTECH
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Fillers Included
- Glass Fiber
- Additives Included
- Heat Stabilizer, Processing Stabilizer
- Heat Stabilizer
- Processing Stabilizer
- Processing Methods
- Injection Molding
- Markets
- Consumer Goods
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- Food Contact Acceptable
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Food Contact Acceptable
- Good Mold Release
- Heat Stabilized
- Processing Stability
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 80-120 °C for 2-3 h; In an air circulatIng dryer 80-120 °C for 2-4 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Construction Applications
- Food Packaging
- Household Goods
- Kitchenware
- Thin-walled Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 3600.0 | MPa | ISO 178 |
| Flexural Strength | 93.0 | MPa | ISO 178 |
| Tensile Modulus | 4200.0 | MPa | ISO 527 |
| Tensile Strength at Break | 65.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 3.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 35.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 19.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 5.0 | kJ/m² | ISO 179/1eA |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1040.0 | kg/m³ | ISO 1183 |
Table 3 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 125.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 139.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 163.0 | °C | ISO 11357 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Mould Temperature | 20 - 70 | °C |
| Melt Temperature | 200 - 250 | °C |
Table 5 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 4.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 230.0 | °C | — |
| MVR Load | 2.16 | kg | — |
| Shrinkage (Lengthwise, 24h) | 0.3 - 0.5 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.5 - 0.7 | % | ISO 294-4 |