ALCOM® PA6 900/11 GF10 MR20 SV12-778MCF
- Chemical Family
- Polyamides
MOCOM Compounds ALCOM® PA6 900/11 GF10 MR20 SV12-778MCF is a pre-dried polyamide 6 containing 10% glass fibers, 20% mineral, and has a silver, metallic effect. It has a low tendency to produce flow lines and low warpage, is highly heat-stabilized and is typically used for automotive and other applications such as housings and engine covers. It is processed by injection molding with a melt temperature of 270-290°C and a mold temperature of 80-100°C.
Product families
Applications
Automotive & Transportation — Automotive
- Powertrain & UTH
Electrical & Electronics — Parts & Components
- Housings & Enclosures
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- ALCOM
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Glass Fiber, Mineral
- Glass Fiber
- Mineral
- Flexural Modulus
- 6000.0 - 6000.0 MPa
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Color
- Silver
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Heat Aging Resistant
- Heat Stabilized
- Low Warpage
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Engine Covers
- Housings
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 6000.0 | MPa | ISO 178 |
| Flexural Strength | 150.0 | MPa | ISO 178 |
| Tensile Modulus | 6100.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 3.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 45.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 4.0 | kJ/m² | ISO 179/1eA |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1440.0 | kg/m³ | ISO 1183 |
Table 3 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 220.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 170.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 219.0 | °C | ISO 11357 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 270 - 290 | °C |
| Mould Temperature | 80 - 100 | °C |
Table 5 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 24.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 275.0 | °C | — |
| MVR Load | 5.0 | kg | — |
| Shrinkage (Lengthwise, 24h) | 0.3 - 0.5 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.6 - 0.8 | % | ISO 294-4 |