ALTECH® PP-H A 2030/157 GF30 CP
- Chemical Family
- PolyolefinsPolypropylenes (PP)
MOCOM Compounds ALTECH® PP-H A 2030/157 GF30 CP is a polypropylene homopolymer suitable for injection molding with a melt temperature of 200-250°C and a mold temperature of 20-70°C. This polypropylene contains 30% glass fibers that have been chemically coupled and heat stabilized, as well as added easy release (demolding) and slip agents. It is suitable for electrical and electronic, building and construction applications and is used in injection molded parts, electrical components, and domestic appliances such as housings, fans, and functional components.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Electronics
- Housings & Enclosures
Product Families
- Polyolefins
Other characteristics
- Brand
- ALTECH
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Fillers Included
- Glass Fiber
- Additives Included
- Heat Stabilizer, Slip Agent
- Heat Stabilizer
- Slip Agent
- Processing Methods
- Injection Molding
- Markets
- Consumer Goods
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Chemically Coupled
- Good Mold Release
- Heat Stabilized
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 80-120 °C for 2-3 h; In an air circulatIng dryer 80-120 °C for 2-4 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Appliances
- Construction Applications
- Electrical Components
- Electrical/Electronic Applications
- Fans
- Housings
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 6100.0 | MPa | ISO 178 |
| Flexural Strength | 120.0 | MPa | ISO 178 |
| Tensile Modulus | 6700.0 | MPa | ISO 527 |
| Tensile Strength at Break | 90.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 3.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 45.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 8.0 | kJ/m² | ISO 179/1eA |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1110.0 | kg/m³ | ISO 1183 |
Table 3 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 135.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 148.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 166.0 | °C | ISO 11357 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Mould Temperature | 20 - 70 | °C |
| Melt Temperature | 200 - 250 | °C |
Table 5 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 15.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 230.0 | °C | — |
| MVR Load | 2.16 | kg | — |
| Shrinkage (Lengthwise, 24h) | 0.2 - 0.4 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.5 - 0.7 | % | ISO 294-4 |