ALTECH® PBT+ABS A 2020/620 GF 20 UV
MOCOM Compounds ALTECH® PBT+ABS A 2020/620 GF 20 UV is a highly UV and heat stabilized base polymer composed of Polybutylene Terephthalate and Acrylonitrile Butadiene Styrene with 20% glass fibers, suitable for various injection molded parts. Pre-drying conditions should be done in a dry air (dessiccant) dryer at a temperature of 90-115°C for 2-4 h depending on moisture content, with a maximum moisture content of less than 0.04%. For processing injection molding, the melt temperature should be between 250-280°C and mold temperature between 60-90°C.
Product families
- Blends & Alloys
Other characteristics
- Brand
- ALTECH
- Density
- 1330.0 - 1330.0 kg/m³
- Features
Heat Aging Resistant, Heat Stabilized, UV Resistant, UV Stabilized
- Functions
- Resin
- Polymer Name
- PBT/ABS Alloy
- Labeling Claims
Azo Colorants-free, Azo Dyes-free, Conflict minerals-free, PAH-free, PFOA-free, PFOS-free, Persistent Organic Pollutants (POP)-free; Azo Colorants-free; Azo Dyes-free; Conflict minerals-free; PAH-free; PFOA-free; PFOS-free; Persistent Organic Pollutants (POP)-free
- Flexural Modulus
- 5600.0 - 5600.0 MPa
- Tensile Strength
- 75.0 - 75.0 MPa
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Fillers Included
- Glass Fiber
- Additives Included
- Heat Stabilizer
- UV Stabilizer
- Material Features
- Heat Aging Resistant
- Heat Stabilized
- UV Resistant
- UV Stabilized
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 90-115 °C for 2-4 h; Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 5600.0 | MPa | ISO 178 |
| Flexural Strength | 115.0 | MPa | ISO 178 |
| Tensile Modulus | 6200.0 | MPa | ISO 527 |
| Tensile Strength at Break | 75.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 2.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 35.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 30.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 3.5 | kJ/m² | ISO 179/1eA |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1330.0 | kg/m³ | ISO 1183 |
Table 3 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 128.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 140.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 226.0 | °C | ISO 11357 |
Table 4 of 6
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.04 | % |
Table 5 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 250 - 280 | °C |
| Mould Temperature | 60 - 90 | °C |
Table 6 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 25.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 260.0 | °C | — |
| MVR Load | 5.0 | kg | — |
| Shrinkage (Lengthwise, 24h) | 0.1 - 0.3 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.3 - 0.5 | % | ISO 294-4 |