ALTECH® PP-H A 4920/200 TV20
- Chemical Family
- PolyolefinsPolypropylenes (PP)
MOCOM Compounds ALTECH® PP-H A 4920/200 TV20 is a Polypropylene Homopolymer base polymer pre-dried in a dry air (dessiccant) dryer or an air circulating dryer at temperatures of 80-120°C for 2-4 hours. It is then processed through injection molding with a melt temperature of 200-250°C and a mold temperature of 20-70°C. It offers benefits such as 20% talcum, good flow, low warpage, easy release (demolding), and slip agent. This material is suitable for electrical and electronic, building and construction, and sport and leisure applications and is used for injection molded parts, interior decoration/finishing, clothing/fasteners, housings, functional components, and different automotive powertrain parts.
Product families
Applications
- Consumer Goods — Sports & Recreation
- Interior
- Powertrain & UTH
- Textile Manufacturing
- Housings & Enclosures
Product Families
- Polyolefins
Other characteristics
- Brand
- ALTECH
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Fillers Included
- Mineral, Talc
- Mineral
- Talc
- Additives Included
- Slip Agent
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Industrial
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Good Flow
- Good Mold Release
- Low Warpage
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 80-120 °C for 2-3 h; In an air circulatIng dryer 80-120 °C for 2-4 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Interior Parts
- Construction Applications
- Electrical/Electronic Applications
- Fasteners
- Housings
- Sporting Goods
- Textile Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2500.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 46.0 | MPa | ISO 178 |
| Tensile Modulus | 2500.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 30.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 4.6 | % | ISO 527 |
| Tensile Elongation at Break | 20.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 30.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 11.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 3.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 2.0 | kJ/m² | ISO 179/1eA |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1070.0 | kg/m³ | ISO 1183 |
Table 3 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 95.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 64.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 163.0 | °C | ISO 11357 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Mould Temperature | 20 - 70 | °C |
| Melt Temperature | 200 - 250 | °C |
Table 5 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 13.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 230.0 | °C | — |
| MVR Load | 2.16 | kg | — |
| Shrinkage (Lengthwise, 24h) | 1.4 - 1.6 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 1 - 1.2 | % | ISO 294-4 |