ALTECH® PS FC 1000/507
- Chemical Family
- Styrenics
MOCOM Compounds ALTECH® PS FC 1000/507 is a white polystyrene impact copolymer used for various packaging applications, suitable for food contact. Pre-drying conditions should be done in a dry air (dessiccant) dryer at 60-75°C for 2-3 hours, or an air circulating dryer at 60-75°C for 2-3 hours. Processing should be done through injection molding, with a melt temperature of 180-260°C and a mold temperature of 10-70°C.
Product families
Applications
Printing & Packaging — Packaging
- Food & Beverage Packaging
Product Families
Plastics — Basic Thermoplastics
- Styrenics
Other characteristics
- Brand
- ALTECH
- Polymer Name
- Polystyrene (unspecified)
- Processing Methods
- Injection Molding
- Color
- White
- Markets
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- Food Contact Acceptable
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Food Contact Acceptable
- High Impact Performance
- Storage Condition
- Store in dry, protected from light.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 60-75 °C for 2-3 h; In an air circulatIng dryer 60-75 °C for 2-3 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Food Packaging
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2000.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 39.0 | MPa | ISO 178 |
| Tensile Modulus | 1900.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 25.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 1.5 | % | ISO 527 |
| Tensile Elongation at Break | 25.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 70.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 60.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 9.5 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 4.0 | kJ/m² | ISO 179/1eA |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1040.0 | kg/m³ | ISO 1183 |
Table 3 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 88.0 | °C | ISO 306 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Mould Temperature | 10 - 70 | °C |
| Melt Temperature | 180 - 260 | °C |
Table 5 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 9.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 200.0 | °C | — |
| MVR Load | 5.0 | kg | — |
| Shrinkage (24h) | 0.4 - 0.7 | % | ISO 294-4 |