ALTECH® PA6 A 1000/520 UV HV
- Chemical Family
- Polyamides
MOCOM Compounds ALTECH® PA6 A 1000/520 UV HV is a Polyamide 6 base polymer that is heat and UV stabilized and fast solidifying with a high viscosity. It is suitable for extruded parts in the building and construction market. Pre-drying conditions should be at 80°C in a dry air (dessiccant) dryer for 2-12 hours depending on moisture content, with a maximum moisture content of 0.15%. For injection molding, it is recommended to use a melt temperature of 250-270°C and a mold temperature of 40-80°C. Additionally, the molding machine should have a large shot capacity and high injection pressure.
Product families
- Polyamides
Other characteristics
- Brand
- ALTECH
- Functions
- Resin
- Polymer Name
- Polyamide 6 (PA 6)
- Labeling Claims
Azo Colorants-free, Azo Dyes-free, Conflict minerals-free, PAH-free, PFOA-free, PFOS-free, Persistent Organic Pollutants (POP)-free; Azo Colorants-free; Azo Dyes-free; Conflict minerals-free; PAH-free; PFOA-free; PFOS-free; Persistent Organic Pollutants (POP)-free
- Additives Included
- Heat Stabilizer, UV Stabilizer
- Heat Stabilizer
- UV Stabilizer
- Processing Methods
- Extrusion, Injection Molding
- Technology
- Plastics
- Material Features
- Fast Solidifying
- Heat Stabilized
- High Viscosity
- UV Resistant
- UV Stabilized
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Construction Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
- Injection Molding
Technical data
Table 1 of 6
18 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 2800.0 | MPa | ISO 178 |
| Flexural Modulus (Conditioned) | 850.0 | MPa | ISO 178 |
| Flexural Stress (Dry, 3.5% Strain) | 90.0 | MPa | ISO 178 |
| Flexural Stress (Conditioned, 3.5% Strain) | 24.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 3250.0 | MPa | ISO 527 |
| Tensile Modulus (Conditioned) | 1100.0 | MPa | ISO 527 |
| Tensile Stress at Yield (Dry) | 84.0 | MPa | ISO 527 |
| Tensile Stress at Yield (Conditioned) | 43.0 | MPa | ISO 527 |
| Tensile Elongation at Yield (Dry) | 3.8 | % | ISO 527 |
| Tensile Elongation at Yield (Conditioned) | 24.0 | % | ISO 527 |
| Tensile Elongation at Break (Dry) | 12.0 | % | ISO 527 |
| Tensile Elongation at Break (Conditioned) | 215.0 | % | ISO 527 |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1140.0 | kg/m³ | ISO 1183 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 63.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 220.0 | °C | ISO 11357 |
Table 4 of 6
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.15 | % |
Table 5 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 250 - 270 | °C |
| Mould Temperature | 40 - 80 | °C |
Table 6 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 1 - 1.2 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 1.2 - 1.4 | % | ISO 294-4 |