ALTECH® PA6 A 2035/509 GF35
- Chemical Family
- Polyamides
MOCOM Compounds ALTECH® PA6 A 2035/509 GF35 is a Polyamide 6 base polymer with a 35% glass fiber filler/additive system heat stabilized for easy release (demolding), good flow, and improved surface appearance. For injection molding, the melt temperature should be between 270-290°C and the mold temperature should be between 80-100°C. When storing, the polymer should be kept dry, protected from light, and not above 30°C. Typical applications of this polymer include injection molded parts.
Product families
- Polyamides
Other characteristics
- Brand
- ALTECH
- Features
Good Flow, Good Mold Release, Good Surface Appearance, Heat Stabilized
- Functions
- Resin
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Glass Fiber
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Good Flow
- Good Mold Release
- Good Surface Appearance
- Heat Stabilized
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 9500.0 | MPa | ISO 178 |
| Flexural Strength (Dry) | 265.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 10500.0 | MPa | ISO 527 |
| Tensile Strength at Break (Dry) | 170.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 3.0 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 80.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Dry, Charpy, at -40°C) | 60.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Dry, Charpy, at 23°C) | 12.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Dry, Charpy, at -40°C) | 9.0 | kJ/m² | ISO 179/1eA |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1400.0 | kg/m³ | ISO 1183 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 210.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 220.0 | °C | ISO 11357 |
Table 4 of 6
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.15 | % |
Table 5 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 270 - 290 | °C |
| Mould Temperature | 80 - 100 | °C |
Table 6 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 0.2 - 0.4 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.6 - 0.8 | % | ISO 294-4 |