ALTECH® PC A 2020/500
- Chemical Family
- Polycarbonate (PC)
MOCOM Compounds ALTECH® PC A 2020/500 is a heat-stabilized, injection-molding grade polycarbonate with 20% glass fibers. It should be pre-dried in a dry air (dessiccant) dryer at temperatures of 100-120°C for 2-3 hours, or in an air circulating dryer at temperatures of 100-120°C for 4-12 hours, depending on the moisture content (which should not exceed 0.02%). The melt temperature for injection-molding should be between 310-330°C, with a mold temperature of 80-130°C. This product is suitable for various applications and market segments and should be stored in a cool, dry place and protected from light, at a temperature not exceeding 30°C.
Product families
- Polycarbonates
Other characteristics
- Brand
- ALTECH
- Features
- Good Mold Release, Heat Stabilized
- Functions
- Resin
- Polymer Name
- Polycarbonate (PC)
- Labeling Claims
Azo Colorants-free, Azo Dyes-free, Conflict minerals-free, PAH-free, PFOA-free, PFOS-free, Persistent Organic Pollutants (POP)-free; Azo Colorants-free; Azo Dyes-free; Conflict minerals-free; PAH-free; PFOA-free; PFOS-free; Persistent Organic Pollutants (POP)-free
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 4200.0 - 4200.0 MPa
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Material Features
- Good Mold Release
- Heat Stabilized
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 100-120 °C for 2-3 h; Dependant on moisture content; In an air circulatIng dryer 100-120 °C for 4-12 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 4200.0 | MPa | ISO 178 |
| Flexural Strength | 110.0 | MPa | ISO 178 |
| Tensile Modulus | 4400.0 | MPa | ISO 527 |
| Tensile Strength at Break | 70.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 3.3 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 45.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 4.0 | kJ/m² | ISO 179/1eA |
Table 2 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1330.0 | kg/m³ | ISO 1183 |
Table 3 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 145.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 138.0 | °C | ISO 75-1/-2 |
Table 4 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.02 | % |
Table 5 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (1.5 mm) | V - 2 | class | UL 94 |
Table 6 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 310 - 330 | °C |
| Mould Temperature | 80 - 130 | °C |
Table 7 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 19.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 300.0 | °C | — |
| MVR Load | 1.2 | kg | — |