ALTECH® PP-H B 4930/506 MR30
- Chemical Family
- PolyolefinsPolypropylenes (PP)
MOCOM Compounds ALTECH® PP-H B 4930/506 MR30 is a Polypropylene Homopolymer that is pre-dried in a dry air (dessiccant) dryer at 80-120°C for 2-3 hours or in an air circulating dryer at 80-120°C for 2-4 hours. It contains 30% talcum and is processing stabilized, heat stabilized, and easy to release (demolding) with a slip agent. It is suitable for injection molding with a melt temperature of 200-250°C and a mold temperature of 20-70°C. It is suitable for use in the Automotive, Machinery and various other markets and is typically used in the production of dashboard/instrument panels, display elements, and various other fixtures/fittings, interiors, and various applications.
Product families
Applications
- Interior
- Displays
Product Families
- Polyolefins
Other characteristics
- Brand
- ALTECH
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Fillers Included
- Mineral, Talc
- Mineral
- Talc
- Additives Included
Heat Stabilizer, Processing Stabilizer, Slip Agent; Heat Stabilizer; Processing Stabilizer; Slip Agent
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Good Mold Release
- Heat Stabilized
- Processing Stability
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 80-120 °C for 2-3 h; In an air circulatIng dryer 80-120 °C for 2-4 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Interior Parts
- Displays
- Fittings
- Fixtures
- Instrument Panel
- Machine/Mechanical Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 3300.0 | MPa | ISO 178 |
| Flexural Strength | 50.0 | MPa | ISO 178 |
| Tensile Modulus | 3200.0 | MPa | ISO 527 |
| Tensile Strength | 30.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 10.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 25.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 10.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 2.5 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 2.5 | kJ/m² | ISO 179/1eA |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1150.0 | kg/m³ | ISO 1183 |
Table 3 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 96.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 80.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 163.0 | °C | ISO 11357 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Mould Temperature | 20 - 70 | °C |
| Melt Temperature | 200 - 250 | °C |
Table 5 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 18.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 230.0 | °C | — |
| MVR Load | 2.16 | kg | — |
| Shrinkage (Lengthwise, 24h) | 0.9 - 1.1 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.7 - 0.9 | % | ISO 294-4 |