ALTECH® PS-HI B 1000/100
- Chemical Family
- High-Impact Polystyrene (HIPS)Styrenics
MOCOM Compounds ALTECH® PS-HI B 1000/100 is a polystyrene-based injection molding grade with special features for electrical and electronic components, suitable for applications such as housings and functional components. It must be kept in a dry, light-protected environment not exceeding 30°C. Pre-drying conditions depend on moisture content and can be done in a dry air (dessiccant) dryer or air circulating dryer at 60-80°C for 2-3 hours. Processing injection molding requires a melt temperature of 180-260°C and a mold temperature of 10-70°C.
Product families
Applications
- Housings & Enclosures
Product Families
- Styrenics
Other characteristics
- Brand
- ALTECH
- Polymer Name
- High Impact Polystyrene (HIPS)
- Processing Methods
- Injection Molding
- Markets
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 60-80 °C for 2-3 h; In an air circulatIng dryer 60-80 °C for 2-3 h; Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Electrical Components
- Electrical/Electronic Applications
- Housings
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 1900.0 | MPa | ISO 178 |
| Flexural Strength | 40.0 | MPa | ISO 178 |
| Tensile Modulus | 1800.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 21.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 1.5 | % | ISO 527 |
| Tensile Elongation at Break | 50.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 100.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 80.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 3.0 | kJ/m² | ISO 179/1eA |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1050.0 | kg/m³ | ISO 1183 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 90.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 70.0 | °C | ISO 75-1/-2 |
Table 4 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (1.5 mm) | HB | class | UL 94 |
| Glow Wire (GWFI, 650°C, 2mm) | Passed | — | DIN EN 60695 |
Table 5 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Mould Temperature | 10 - 70 | °C |
| Melt Temperature | 180 - 260 | °C |
Table 6 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 12.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 200.0 | °C | — |
| MVR Load | 5.0 | kg | — |
| Shrinkage (24h) | 0.3 - 0.6 | % | ISO 294-4 |