ALTECH® PP-H A 1000/100 DS
- Chemical Family
- PolyolefinsPolypropylenes (PP)
MOCOM Compounds ALTECH® PP-H A 1000/100 DS is a polypropylene homopolymer suitable for injection molding with a melt temperature of 200-240°C and a mold temperature of 20-70°C. Additionally, this product contains an antioxidant, lubricant, detergent solution stabilizer, high heat stabilizer, and slip agent which allows for easy release (demolding) and good hydrolysis resistance. It is suitable for various market segments, machinery, and application areas such as injection molded parts. This product should be stored in a dry place, protected from light, and at a temperature not exceeding 30°C.
Product families
- Polyolefins
Other characteristics
- Brand
- ALTECH
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Additives Included
Antioxidant, Heat Stabilizer, Lubricant (Unspecified), Slip Agent; Antioxidant; Heat Stabilizer; Lubricant (Unspecified); Slip Agent
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Anti-Oxidant
- Detergent Stabilised
- Excellent Hydrolysis Resistance
- Good Mold Release
- Heat Aging Resistant
- Heat Stabilized
- Lubricated
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 80-120 °C for 2-3 h; In an air circulatIng dryer 80-120 °C for 2-4 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Machine/Mechanical Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 1300.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 33.0 | MPa | ISO 178 |
| Tensile Modulus | 1500.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 34.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 10.0 | % | ISO 527 |
| Tensile Elongation at Break | 80.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | no break | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 5.0 | kJ/m² | ISO 179/1eA |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 900.0 | kg/m³ | ISO 1183 |
Table 3 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 89.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 61.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 168.0 | °C | ISO 11357 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Mould Temperature | 20 - 70 | °C |
| Melt Temperature | 200 - 240 | °C |
Table 5 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 3.8 | cm³/10min | ISO 1133 |
| MVR Temperature | 230.0 | °C | — |
| MVR Load | 2.16 | kg | — |
| Shrinkage (Lengthwise, 24h) | 1.6 - 2 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 1.4 - 1.8 | % | ISO 294-4 |