To catalogue
ALTECH® PBT A 1000/106
- Chemical Family
- Polyesters
MOCOM Compounds ALTECH® PBT A 1000/106 is a polybutylene terephthalate base polymer that is heat stabilized and has easy release (demolding) properties. It is used in various market segments for injection molded parts. For injection molding, melt temperature should be between 250-270°C and mold temperature should be between 40-70°C.
Product families
Plastics — Engineering & Specialty Polymers
- Polyesters & Copolyesters
Other characteristics
- Brand
- ALTECH
- Features
- Good Mold Release, Heat Stabilized
- Functions
- Resin
- Polymer Name
- Polybutylene Terephthalate (PBT)
- Flexural Modulus
- 2600.0 - 2600.0 MPa
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Good Mold Release
- Heat Stabilized
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 100-120 °C for 2-4 h; In an air circulatIng dryer 100-120 °C for 4-8 h; Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2600.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 80.0 | MPa | ISO 178 |
| Tensile Modulus | 2500.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 58.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 3.2 | % | ISO 527 |
| Tensile Elongation at Break | 40.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 200.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 150.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 3.0 | kJ/m² | ISO 179/1eA |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1350.0 | kg/m³ | ISO 1183 |
Table 3 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 180.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 55.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 225.0 | °C | ISO 11357 |
Table 4 of 6
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.04 | % |
Table 5 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 250 - 270 | °C |
| Mould Temperature | 40 - 70 | °C |
Table 6 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 15.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 250.0 | °C | — |
| MVR Load | 2.16 | kg | — |
| Shrinkage (Lengthwise, 24h) | 1.9 - 2.3 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 1.8 - 2.2 | % | ISO 294-4 |