ALTECH® PP-H A 2045/500
- Chemical Family
- PolyolefinsPolypropylenes (PP)
MOCOM Compounds ALTECH® PP-H A 2045/500 is a Polypropylene Homopolymer with 45% glass fibers, heat stabilized, extrusion grade, low emission, and processing stabilized. It is suitable for Pre-Drying Conditions in an air circulating dryer 80-120°C for 2-4 h, or in a dry air (dessiccant) dryer 80-120°C for 2-3 h. Processing Injection molding is done at a melt temperature of 200-250°C and a mold temperature of 20-70°C. This product is used for building and construction, sport and leisure applications, such as functional components, housings, and sports equipment. It should not be exposed to strong UV radiation and should not be stored in direct sunlight.
Product families
Applications
- Consumer Goods — Sports & Recreation
- EIFS & Insulation
- Housings & Enclosures
Product Families
- Polyolefins
Other characteristics
- Brand
- ALTECH
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Fillers Included
- Glass Fiber
- Additives Included
- Heat Stabilizer, Processing Stabilizer
- Heat Stabilizer
- Processing Stabilizer
- Processing Methods
- Extrusion, Injection Molding
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Heat Stabilized
- Low Emissions
- Processing Stability
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 80-120 °C for 2-3 h; In an air circulatIng dryer 80-120 °C for 2-4 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Construction Applications
- Housings
- Sporting Goods
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
- Injection Molding
Technical data
Table 1 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 7800.0 | MPa | ISO 178 |
| Flexural Strength | 100.0 | MPa | ISO 178 |
| Tensile Modulus | 8600.0 | MPa | ISO 527 |
| Tensile Strength at Break | 67.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 1.7 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 20.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 7.0 | kJ/m² | ISO 179/1eA |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1270.0 | kg/m³ | ISO 1183 |
Table 3 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 114.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 147.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 168.0 | °C | ISO 11357 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Mould Temperature | 20 - 70 | °C |
| Melt Temperature | 200 - 250 | °C |
Table 5 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 2.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 230.0 | °C | — |
| MVR Load | 2.16 | kg | — |
| Shrinkage (Lengthwise, 24h) | 0.2 - 0.4 | % | ISO 294-4 |