ALTECH® PA66 A 2030/109 GF30
- Chemical Family
- Polyamides
MOCOM Compounds ALTECH® PA66 A 2030/109 GF30 is a heat stabilized, easy release and easy flow polyamide 66 with a 30% glass fiber filler/additive system. It has pre-drying conditions of 80°C in a dry air (dessiccant) dryer for 2-12 h depending on moisture content, with a maximum moisture content of <0.15%. The processing injection molding melt temperature is 280-300°C, and the mold temperature is 80-120°C. This market segment is for automotive use, and is typically used for applications such as housings and different automotive powertrain parts. It must be stored in a cool and dark environment, not exceeding 30°C.
Product families
Applications
- Exterior & Body
- Interior
- Powertrain & UTH
- Housings & Enclosures
Product Families
- Polyamides
Other characteristics
- Brand
- ALTECH
- End Uses
Automotive Applications, Automotive Exterior Parts, Automotive Interior Parts, Housings
- Features
- Good Flow, Good Mold Release, Heat Stabilized
- Functions
- Resin
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Fiber
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Good Flow
- Good Mold Release
- Heat Stabilized
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Exterior Parts
- Automotive Interior Parts
- Housings
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 8500.0 | MPa | ISO 178 |
| Flexural Modulus (Conditioned) | 6000.0 | MPa | ISO 178 |
| Flexural Strength (Dry) | 250.0 | MPa | ISO 178 |
| Flexural Strength (Conditioned) | 185.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 10000.0 | MPa | ISO 527 |
| Tensile Modulus (Conditioned) | 6400.0 | MPa | ISO 527 |
| Tensile Strength at Break (Dry) | 180.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 3.1 | % | ISO 527 |
| Tensile Strength at Break (Conditioned) | 110.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Conditioned) | 5.5 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 55.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Conditioned, Charpy, at 23°C) | 75.0 | kJ/m² | ISO 179/1eU |
Table 2 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1360.0 | kg/m³ | ISO 1183 |
Table 3 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 250.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 263.0 | °C | ISO 11357 |
Table 4 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.15 | % |
Table 5 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (Dry, 0.75 mm) | HB | class | UL 94 |
| UL Recognition (Dry) | yes | — | — |
Table 6 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 280 - 300 | °C |
| Mould Temperature | 80 - 120 | °C |
Table 7 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 0.2 - 0.4 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.7 - 0.9 | % | ISO 294-4 |