ALTECH® PA66 A 1000/109
- CAS Number
- 280-57-9
- Chemical Family
- Polyamides
MOCOM Compounds ALTECH® PA66 A 1000/109 is a polyamide 66 heat stabilized, easy flow and easy release (demolding) base polymer. It is suitable for pre-drying conditions at 80°C in a dry air (dessiccant) dryer for 2-12 h depending on moisture content, with a maximum moisture content of 0.15%. It can be used in a variety of applications in automotive, electrical, and electronic market segments, such as electrical components, interior decoration/finishing, exterior parts, and various automotive powertrain parts.
Product families
Applications
- Exterior & Body
- Interior
- Powertrain & UTH
Product Families
- Polyamides
Other characteristics
- Brand
- ALTECH
- Synonyms
1,4-Diazabicyclo[2.2.2]octane,1,4-Ethylenepiperazine
- Functions
- Resin
- Polymer Name
- Polyamide 66 (PA 66)
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Good Flow
- Good Mold Release
- Heat Stabilized
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Exterior Parts
- Automotive Interior Parts
- Electrical Components
- Electrical/Electronic Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
17 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 3000.0 | MPa | ISO 178 |
| Flexural Modulus (Conditioned) | 1300.0 | MPa | ISO 178 |
| Flexural Stress (Dry, 3.5% Strain) | 95.0 | MPa | ISO 178 |
| Flexural Stress (Conditioned, 3.5% Strain) | 40.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 3300.0 | MPa | ISO 527 |
| Tensile Modulus (Conditioned) | 1500.0 | MPa | ISO 527 |
| Tensile Stress at Yield (Dry) | 88.0 | MPa | ISO 527 |
| Tensile Stress at Yield (Conditioned) | 58.0 | MPa | ISO 527 |
| Tensile Elongation at Yield (Dry) | 4.1 | % | ISO 527 |
| Tensile Elongation at Yield (Conditioned) | 20.0 | % | ISO 527 |
| Tensile Elongation at Break (Dry) | 20.0 | % | ISO 527 |
| Tensile Elongation at Break (Conditioned) | 125.0 | % | ISO 527 |
Table 2 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1130.0 | kg/m³ | ISO 1183 |
Table 3 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 79.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 264.0 | °C | ISO 11357 |
Table 4 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.15 | % |
Table 5 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (Dry, 1.5 mm) | V - 2 | class | UL 94 |
| Flammability (Dry, 3 mm) | V - 2 | class | UL 94 |
Table 6 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 270 - 290 | °C |
| Mould Temperature | 40 - 80 | °C |
Table 7 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 1.6 - 2.2 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 1.6 - 2.2 | % | ISO 294-4 |