ALTECH® PA66 A 2050/100 GF50
- CAS Number
- 9002-93-1
- Chemical Family
- Polyamides
MOCOM Compounds ALTECH® PA66 A 2050/100 GF50 is a heat-stabilized, easy-release polyamide 66 with 50% glass fiber content, suitable for use in automotive applications, machinery, and injection-molded parts, interior decoration/finishing, and functional components. The recommended processing injection molding melt temperature is 280-300°C and the recommended mold temperature is 80-120°C.
Product families
Applications
- Interior
Product Families
- Polyamides
Other characteristics
- Brand
- ALTECH
- Functions
- Resin
- Polymer Name
- Polyamide 66 (PA 66)
- Labeling Claims
Azo Colorants-free, Azo Dyes-free, Conflict minerals-free, PAH-free, PFOA-free, PFOS-free, Persistent Organic Pollutants (POP)-free; Azo Colorants-free; Azo Dyes-free; Conflict minerals-free; PAH-free; PFOA-free; PFOS-free; Persistent Organic Pollutants (POP)-free
- Fillers Included
- Glass Fiber
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Technology
- Plastics
- Material Features
- Good Mold Release
- Heat Stabilized
- High Stiffness
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Interior Parts
- Machine/Mechanical Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 15000.0 | MPa | ISO 178 |
| Flexural Modulus (Conditioned) | 13500.0 | MPa | ISO 178 |
| Flexural Strength (Dry) | 340.0 | MPa | ISO 178 |
| Flexural Strength (Conditioned) | 295.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 16500.0 | MPa | ISO 527 |
| Tensile Modulus (Conditioned) | 15000.0 | MPa | ISO 527 |
| Tensile Strength at Break (Dry) | 230.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 2.5 | % | ISO 527 |
| Tensile Strength at Break (Conditioned) | 195.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Conditioned) | 2.5 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 90.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Conditioned, Charpy, at 23°C) | 80.0 | kJ/m² | ISO 179/1eU |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1560.0 | kg/m³ | ISO 1183 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 256.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 264.0 | °C | ISO 11357 |
Table 4 of 6
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.15 | % |
Table 5 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 280 - 300 | °C |
| Mould Temperature | 80 - 120 | °C |
Table 6 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 0.1 - 0.3 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.5 - 0.7 | % | ISO 294-4 |