ALTECH® PA6 A 3230/500 GB15 GF15
- Chemical Family
- Polyamides
MOCOM Compounds ALTECH® PA6 A 3230/500 GB15 GF15 is a heat-stabilized polyamide 6 base polymer with a glass fiber/glass bead filler/additive system. It is suitable for various market segments and applications. Pre-drying in a dry air (dessiccant) dryer at 60-80°C for 2-12 hours, depending on moisture content, is necessary before injection molding at a melt temperature of 260-290°C and a mold temperature of 80-100°C. It should be stored in a dark place and kept at a temperature no higher than 30°C.
Product families
- Polyamides
Other characteristics
- Brand
- ALTECH
- Functions
- Resin
- Polymer Name
- Polyamide 6 (PA 6)
- Labeling Claims
Azo Colorants-free, Azo Dyes-free, Conflict minerals-free, PAH-free, PFOA-free, PFOS-free, Persistent Organic Pollutants (POP)-free; Azo Colorants-free; Azo Dyes-free; Conflict minerals-free; PAH-free; PFOA-free; PFOS-free; Persistent Organic Pollutants (POP)-free
- Fillers Included
- Glass Bead/Glass Fiber
- Flexural Modulus
- 6000.0 - 6000.0 MPa
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Certifications & Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS), EC No.1907/2006, IATF 16949, ISO 13485, ISO 14001, ISO 17025, ISO 45001, ISO 50001, ISO 9001, REACH (Europe), REACH (UK), RoHS Compliant, SVHC Compliant
- Technology
- Plastics
- Material Features
- Heat Stabilized
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 60-80 °C for 2-12 h; Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 6000.0 | MPa | ISO 178 |
| Flexural Strength | 174.0 | MPa | ISO 178 |
| Tensile Modulus | 6000.0 | MPa | ISO 527 |
| Tensile Strength at Break | 110.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 2.9 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 40.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 35.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 4.5 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 4.0 | kJ/m² | ISO 179/1eA |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1360.0 | kg/m³ | ISO 1183 |
Table 3 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (1.8 MPa) | 202.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point) | 220.0 | °C | ISO 11357 |
Table 4 of 5
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 260 - 290 | °C |
| Mould Temperature | 80 - 100 | °C |
Table 5 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 0.3 - 0.5 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.7 - 0.9 | % | ISO 294-4 |