ALTECH® PA6 A 1000/209
- Chemical Family
- Polyamides
MOCOM Compounds ALTECH® PA6 A 1000/209 is a polyamide 6 base polymer with easy release (demolding), easy flow, and fast solidifying properties, and is heat stabilized. It is suitable for electrical and electronic components and injection molded parts such as thin walled parts, protection caps, and functional components. Pre-drying Conditions should be 80°C in a dry air (dessiccant) dryer for 2-12 hours depending on moisture content, with a maximum moisture content of <0.15%. Processing Injection molding should use a melt temperature of 250-270°C and a mold temperature of 40-80°C. It should be stored dry and protected from light, not exceeding 30°C.
Product families
- Polyamides
Other characteristics
- Brand
- ALTECH
- Features
Fast Solidifying, Good Flow, Good Mold Release, Heat Stabilized
- Functions
- Resin
- Polymer Name
- Polyamide 6 (PA 6)
- Labeling Claims
Azo Colorants-free, Azo Dyes-free, Conflict minerals-free, PAH-free, PFOA-free, PFOS-free, Persistent Organic Pollutants (POP)-free; Azo Colorants-free; Azo Dyes-free; Conflict minerals-free; PAH-free; PFOA-free; PFOS-free; Persistent Organic Pollutants (POP)-free
- Additives Included
- Heat Stabilizer
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Material Features
- Fast Solidifying
- Good Flow
- Good Mold Release
- Heat Stabilized
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-12 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Electrical Components
- Electrical/Electronic Applications
- Protective Caps
- Thin-walled Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 2800.0 | MPa | ISO 178 |
| Flexural Stress (Dry, 3.5% Strain) | 95.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 3200.0 | MPa | ISO 527 |
| Tensile Stress at Yield (Dry) | 90.0 | MPa | ISO 527 |
| Tensile Elongation at Yield (Dry) | 3.8 | % | ISO 527 |
| Tensile Elongation at Break (Dry) | 15.0 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | no break | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Dry, Charpy, at 23°C) | 4.0 | kJ/m² | ISO 179/1eA |
Table 2 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1130.0 | kg/m³ | ISO 1183 |
Table 3 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 65.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 220.0 | °C | ISO 11357 |
Table 4 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.15 | % |
Table 5 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (Dry, 1.5 mm) | V - 2 | class | UL 94 |
| UL Recognition (Dry) | yes | — | — |
Table 6 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 250 - 270 | °C |
| Mould Temperature | 40 - 80 | °C |
Table 7 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 1.2 - 1.4 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 1.2 - 1.4 | % | ISO 294-4 |