ALTECH® B PA6/6T B 4030/219 MR30 IM
- Chemical Family
- Polyamides
MOCOM Compounds ALTECH® B PA6/6T B 4030/219 MR30 IM is a polyphthalamide-based polymer with 30% mineral filler/additive system, elastomer modified, heat-stabilized, and processing-stabilized, providing easy release (demolding). It is suitable for injection molding with a melt temperature range of 310-330°C and a mold temperature range of 70-100°C. It is used in the machinery market segment for injection-molded parts and functional components. Pre-drying conditions should be 110°C in a dry air (dessiccant) dryer for 4-8 hours with a maximum moisture content of <0.03%.
Product families
- Polyamides
Other characteristics
- Brand
- ALTECH
- End Uses
- Machine/Mechanical Parts
- Features
Elastomer Modified, Good Mold Release, Heat Stabilized, Processing Stability
- Functions
- Resin
- Polymer Name
- Polyphthalamide (PPA)
- Fillers Included
- Mineral
- Additives Included
- Heat Stabilizer, Processing Stabilizer
- Heat Stabilizer
- Processing Stabilizer
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Labeling Claims
- Azo Colorants-free
- Azo Dyes-free
- Conflict minerals-free
- PAH-free
- PFOA-free
- PFOS-free
- Persistent Organic Pollutants (POP)-free
- Material Features
- Elastomer Modified
- Good Mold Release
- Heat Stabilized
- Processing Stability
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
- 110 °C in a dry air (dessiccant) dryer for 4-8 h
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Machine/Mechanical Parts
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
17 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus (Dry) | 4000.0 | MPa | ISO 178 |
| Flexural Modulus (Conditioned) | 4200.0 | MPa | ISO 178 |
| Flexural Stress (Dry, 3.5% Strain) | 95.0 | MPa | ISO 178 |
| Flexural Strength (Conditioned) | 94.0 | MPa | ISO 178 |
| Tensile Modulus (Dry) | 4000.0 | MPa | ISO 527 |
| Tensile Modulus (Conditioned) | 4100.0 | MPa | ISO 527 |
| Tensile Stress at Yield (Conditioned) | 55.0 | MPa | ISO 527 |
| Tensile Elongation at Yield (Conditioned) | 3.8 | % | ISO 527 |
| Tensile Strength at Break (Dry) | 62.0 | MPa | ISO 527 |
| Tensile Elongation at Break (Dry) | 4.1 | % | ISO 527 |
| Tensile Elongation at Break (Conditioned) | 5.0 | % | ISO 527 |
| Impact Strength (Dry, Charpy, at 23°C) | 90.0 | kJ/m² | ISO 179/1eU |
Table 2 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density (Dry) | 1360.0 | kg/m³ | ISO 1183 |
Table 3 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| HDT / A (Dry, 1.8 MPa) | 98.0 | °C | ISO 75-1/-2 |
| DSC (Melt Point, Dry) | 302.0 | °C | ISO 11357 |
Table 4 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.03 | % |
Table 5 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (Dry, 1.5 mm) | HB | class | UL 94 |
| UL Recognition (Dry) | yes | — | — |
Table 6 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 310 - 330 | °C |
| Mould Temperature | 70 - 100 | °C |
Table 7 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Shrinkage (Lengthwise, 24h) | 1.1 - 1.5 | % | ISO 294-4 |
| Shrinkage (Lateral, 24h) | 0.9 - 1.3 | % | ISO 294-4 |