ALTECH® ABS A 2010/500 GF10
MOCOM Compounds ALTECH® ABS A 2010/500 GF10 is a base polymer composed of Acrylonitrile/Butadiene/Styrene/Copolymer with 10% glass fibers. It has good flow, slip agent, and processing stabilization properties. This injection molding grade has a melt temperature of 220-260°C and a mold temperature of 50-80°C. Pre-drying conditions should be 80°C in a dry air (dessiccant) dryer for 2-4 hours and 80°C in an air circulating dryer for 3-6 hours depending on moisture content, with a maximum moisture content of 0.20%. It has various market segments and application areas for injection molded parts and should be protected from light and stored at temperatures not exceeding 30°C.
Product families
- Styrenics
Other characteristics
- Brand
- ALTECH
- Features
Good Flow, Heat Aging Resistant, Processing Stability
- Functions
- Resin
- Polymer Name
- Acrylonitrile Butadiene Styrene (ABS)
- Labeling Claims
Azo Colorants-free, Azo Dyes-free, Conflict minerals-free, PAH-free, PFOA-free, PFOS-free, Persistent Organic Pollutants (POP)-free; Azo Colorants-free; Azo Dyes-free; Conflict minerals-free; PAH-free; PFOA-free; PFOS-free; Persistent Organic Pollutants (POP)-free
- Fillers Included
- Glass Fiber
- Additives Included
- Processing Stabilizer, Slip Agent
- Processing Stabilizer
- Slip Agent
- Processing Methods
- Injection Molding
- Technology
- Plastics
- Material Features
- Good Flow
- Heat Aging Resistant
- Processing Stability
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
- 80 °C in a dry air (dessiccant) dryer for 2-4 h
- 80 °C in an air circulating dryer for 3-6 h
- Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 4000.0 | MPa | ISO 178 |
| Flexural Strength | 80.0 | MPa | ISO 178 |
| Tensile Modulus | 4300.0 | MPa | ISO 527 |
| Tensile Strength at Break | 53.0 | MPa | ISO 527 |
| Tensile Elongation at Break | 1.8 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 16.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 20.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Ball Indentation Hardness (H358/30) | 120.0 | MPa | ISO 2039-1 |
Table 2 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1140.0 | kg/m³ | ISO 1183 |
Table 3 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 97.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 91.0 | °C | ISO 75-1/-2 |
Table 4 of 7
1 row| Characteristic | Value | Unit |
|---|---|---|
| Moisture Content | max. 0.2 | % |
Table 5 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flammability (1.5 mm) | HB | class | UL 94 |
| Glow Wire (GWFI, 650°C, 2mm) | Passed | — | DIN EN 60695 |
Table 6 of 7
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 220 - 260 | °C |
| Mould Temperature | 50 - 80 | °C |
Table 7 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 15.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 220.0 | °C | — |
| MVR Load | 10.0 | kg | — |