ALTECH® ABS A 2015/506 GF15

Chemical Family: Acrylonitrile Butadiene Styrene (ABS), StyrenicsAcrylonitrile Butadiene Styrene (ABS)Styrenics

MOCOM Compounds ALTECH® ABS A 2015/506 GF15 is a copolymer of Acrylonitrile/Butadiene/Styrene with 15% glass fibers as a filler/additive system. It is an injection molding grade with processing stabilization, suitable for various injection molded parts. Before processing, the material should be pre-dried to a maximum moisture content of <0,20%. Pre-drying conditions involve 80°C in a dry air (dessiccant) dryer for 2-4 hours and 80°C in an air circulating dryer for 3-6 hours, depending on moisture content. For injection molding, melt temperature should be between 220-260°C and mold temperature should be between 50-80°C.

Product families

Plastics — Basic Thermoplastics

Styrenics

Other characteristics

Brand: ALTECH
Features: Processing Stability
Functions: Resin
Polymer Name: Acrylonitrile Butadiene Styrene (ABS)
Labeling Claims: Azo Colorants-free, Azo Dyes-free, Conflict minerals-free, PAH-free, PFOA-free, PFOS-free, Persistent Organic Pollutants (POP)-free; Azo Colorants-free; Azo Dyes-free; Conflict minerals-free; PAH-free; PFOA-free; PFOS-free; Persistent Organic Pollutants (POP)-free
Fillers Included: Glass Fiber
Additives Included: Processing Stabilizer
Processing Methods: Injection Molding
Technology: Plastics
Material Features: Processing Stability
Storage Condition: Store in dry, protected from light not above 30°C.
Pre-Drying Conditions: 80 °C in a dry air (dessiccant) dryer for 2-4 h
80 °C in an air circulating dryer for 3-6 h
Dependant on moisture content
Certifications and Compliance: Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 6

10 rows

Characteristic	Value	Unit	Method
Flexural Modulus	4500.0	MPa	ISO 178
Flexural Strength	88.0	MPa	ISO 178
Tensile Modulus	4900.0	MPa	ISO 527
Tensile Strength at Break	60.0	MPa	ISO 527
Tensile Elongation at Break	1.7	%	ISO 527
Impact Strength (Charpy, at 23°C)	18.0	kJ/m²	ISO 179/1eU
Impact Strength (Charpy, at -40°C)	15.0	kJ/m²	ISO 179/1eU
Notched Impact Strength (Charpy, at 23°C)	7.0	kJ/m²	ISO 179/1eA
Notched Impact (Charpy, at -40°C)	5.0	kJ/m²	ISO 179/1eA
Ball Indentation Hardness (H358/30)	120.0	MPa	ISO 2039-1

Table 2 of 6

1 row

Characteristic	Value	Unit	Method
Density	1140.0	kg/m³	ISO 1183

Table 3 of 6

2 rows

Characteristic	Value	Unit	Method
Vicat B50	102.0	°C	ISO 306
HDT / A (1.8 MPa)	102.0	°C	ISO 75-1/-2