ALTECH® ABS+PMMA A 1000/500
MOCOM Compounds ALTECH® ABS+PMMA A 1000/500 is a processing-stabilized, scratch-resistant polymer used for injection molded parts in various market segments, such as clothing/fasteners and bezels. It has a service temperature range of -40-85°C and a maximum shelf life of 24 months. Pre-drying conditions should be implemented before processing at a melt temperature of 220-260°C and a mold temperature of 50-80°C. The base polymer is polymethylmethacrylate and acrylonitrile/butadiene/styrene/copolymer. It should be stored dry and protected from light at temperatures not exceeding 30°C.
Product families
Applications
- Textile Manufacturing
Product Families
- Blends & Alloys
Other characteristics
- Brand
- ALTECH
- Density
- 1100.0 - 1100.0 kg/m³
- Features
- Good Scratch Resistance, Processing Stability
- Functions
- Resin
- Polymer Name
- ABS/PMMA Alloy
- Labeling Claims
Azo Colorants-free, Azo Dyes-free, Conflict minerals-free, PAH-free, PFOA-free, PFOS-free, Persistent Organic Pollutants (POP)-free; Azo Colorants-free; Azo Dyes-free; Conflict minerals-free; PAH-free; PFOA-free; PFOS-free; Persistent Organic Pollutants (POP)-free
- Flexural Modulus
- 2750.0 - 2750.0 MPa
- Processing Methods
- Injection Molding
- Markets
- Industrial
- Shelf LIfe
- Minimum 24 months
- Technology
- Plastics
- Additives Included
- Processing Stabilizer
- Material Features
- Good Scratch Resistance
- Processing Stability
- Storage Condition
Store in dry, protected from light not above 30°C.
- Pre-Drying Conditions
In a dry air (dessiccant) dryer 65-90 °C for 3-4 h; In an air circulatIng dryer 65-90 °C for 4-6 h; Dependant on moisture content
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); EC No.1907/2006; IATF 16949; ISO 13485; ISO 14001; ISO 17025; ISO 45001; ISO 50001; ISO 9001; REACH (Europe); REACH (UK); RoHS Compliant; SVHC Compliant
- Plastics and Elastomers End Uses
- Bezels
- Fasteners
- Textile Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | 2750.0 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 75.0 | MPa | ISO 178 |
| Tensile Modulus | 2600.0 | MPa | ISO 527 |
| Tensile Stress at Yield | 52.0 | MPa | ISO 527 |
| Tensile Elongation at Yield | 2.5 | % | ISO 527 |
| Tensile Elongation at Break | 22.0 | % | ISO 527 |
| Impact Strength (Charpy, at 23°C) | 48.0 | kJ/m² | ISO 179/1eU |
| Impact Strength (Charpy, at -40°C) | 45.0 | kJ/m² | ISO 179/1eU |
| Notched Impact Strength (Charpy, at 23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Notched Impact (Charpy, at -40°C) | 3.0 | kJ/m² | ISO 179/1eA |
| Ball Indentation Hardness (H358/30) | 125.0 | MPa | ISO 2039-1 |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1100.0 | kg/m³ | ISO 1183 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat B50 | 95.0 | °C | ISO 306 |
| HDT / A (1.8 MPa) | 81.0 | °C | ISO 75-1/-2 |
Table 4 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Service Temperature (depending on load, geometry, etc.) | - 40 to 85 | °C |
| Moisture Content | max. 0.02 | % |
Table 5 of 6
2 rows| Characteristic | Value | Unit |
|---|---|---|
| Melt Temperature | 220 - 260 | °C |
| Mould Temperature | 50 - 80 | °C |
Table 6 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Index (MVR) | 25.0 | cm³/10min | ISO 1133 |
| MVR Temperature | 220.0 | °C | — |
| MVR Load | 10.0 | kg | — |
| Shrinkage (24h) | 0.5 - 0.8 | % | ISO 294-4 |